HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
566 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

Preliminary

T5 GF 50 6 black (8000)

PPA GF50

Standard Grade with good surface quality. AKROMID® T5 GF 50 6 black (8000) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up


Modulus

18.500MPa

Strength

260MPa

Impact

65kJ/m²

Standard Grade with good surface quality. AKROMID® T5 GF 50 6 black (8000) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up

AKROMID®

UL

A3 GF 30 HU natural (6661)

PA66 GF30

AKROMID® A3 GF 30 HU natural (6661) - PA 6.6 30% glass fiber reinforced, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and in the automotive industry


Modulus

10.500MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 HU natural (6661) - PA 6.6 30% glass fiber reinforced, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and in the automotive industry

AKROTEK®

UL

PK-VM GF 30 FR orange (8537)

PK GF30 FR(40)

AKROTEK® PK-VM GF 30 FR orange (8537) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.


Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 30 FR orange (8537) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.

AKROMID®

UL
Preliminary

B28 GF 30 9 FR orange (8645)

PA6 GF30 FR(40)

AKROMID® B28 GF 30 9 FR orange (8645) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.


Modulus

10.200MPa

Strength

138MPa

Impact

70kJ/m²

AKROMID® B28 GF 30 9 FR orange (8645) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

AKROTEK®

PK-VM GF 30 black (8655)

PK GF30

AKROTEK® PK-VM GF 30 black (8655) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance


Modulus

8.500MPa

Strength

130MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 30 black (8655) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

PRECITE®

Preliminary

K GF 30 4 LA ECO black (8699)

PBT-PET- GF 30

PRECITE® K GF 30 4 ECO black (8699) - PBT/PET blend, regenerated post-consumer PET, glass fibre, hydrolysis stabillised, high strength, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.


Modulus

9.500MPa

Strength

120MPa

Impact

65kJ/m²

PRECITE® K GF 30 4 ECO black (8699) - PBT/PET blend, regenerated post-consumer PET, glass fibre, hydrolysis stabillised, high strength, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROTEK®

Preliminary

PK-VM GF 15 black (8686)

PK GF15

AKROTEK® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance


Modulus

4.500MPa

Strength

90MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID®

B28 GM 5/25 FR black (7492)PA6 (GF5+GB25) FR(40)

AKROMID® B28 GM 5/25 FR black (7492) is a flame retardant PA6, reinforced with 5% glass fibres and 25% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS and melamine. Due to its good flowability, it is characterised by easy processability as well as good surface properties. The product is suitable for enclosure applications in the E&E industry due to its low warpage, high stiffness and strength.

Features

flame retardant
recycled content
low warpage
easy flow
E&E

Properties

Modulus

5.000MPa

Strength

55MPa

Impact

30kJ/m²

Sustainability


Recycled content

25 %

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
5000 MPa
3000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
55 MPa
35 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,6 %
5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30 kJ/m²

Thermal Properties


Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability


Flammability

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class

General Properties


Density

ISO 1183

23°C
1,39 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,4 - 1,6 %

Molding shrinkage

ISO 294-4

flow
transverse
0,65 - 0,85 %
0,75 - 0,95 %

Electrical Properties


Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.