PC ICF 20 AM ECO black (9159) PC CF20

AKROTEK® PC ICF 20 AM ECO black (9159) is a recycled Polycarbonate reinforced with 20 % carbon fiber. This material is optimized for additive manufacturing (3D printing) and large format additive manufacturing (LFAM). The use temperature of 130 °C qualifies it for printing tooling and molds for CFRP and autoclave use. It features a wide processing window, easy printability and post processing. The formulations of the environment-friendly ECO products are partly based on regenerated postindustrial feedstock saving valuable natural resources and therefore contributes to a low carbon foot print.

Features

3D printing / additive manufacturing
reused content

Properties

Modulus

13.700MPa

Strength

155MPa

Impact

45kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
13700 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
155 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,4 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
45 kJ/m²

General Properties

Density

ISO 1183

23°C
1,28 g/cm³

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

PRECITE®

P3 ICF 20 black (6947)

PBT CF20

PRECITE® P3 ICF 20 black (6947) is a PBT reinforced with 20% carbon fiber with excellent dimensional stability. Thanks to its low moisture absorption, PRECITE® achieves consistent mechanical and electrical properties, even under changing climatic co

Modulus

16.000MPa

Strength

150MPa

Impact

50kJ/m²

AKROTEK®

Preliminary

ABS ICF 20 AM black (8722)

ABS CF20

AKROTEK® ABS ICF 20 AM black (8722) is an acrylonitrile butadiene styrene copolymer reinforced with 20 % carbon fiber. It is characterized by medium stiffness and strength. The compound is optimized for pellet-based additive manufacturing (3D printin

Modulus

13.400MPa

Strength

100MPa

Impact

20kJ/m²

AKROTEK®

Preliminary

ASA ICF 20 AM black (8723)

ASA CF20

AKROTEK® ASA ICF 20 AM black (8723) is an acrylonitrile styrene acrylate with 20 % carbon fiber for reinforcement. It is characterized by medium stiffness and strength. The compound is optimized for pellet-based additive manufacturing (3D printing) a

Modulus

13.400MPa

Strength

105MPa

Impact

25kJ/m²

AKROLEN®

Preliminary

NEXT PP ICF 20 AM black (8759BMBCI)

PP CF20

AKROLEN® NEXT PP ICF 20 AM black (8759BMBCI) is a biomass-balanced polypropylene with 20% carbon fiber reinforcement. It is characterized by low density as well as medium stiffness and strength. The material is suitable for water contact applications

Modulus

8.100MPa

Strength

60MPa

Impact

45kJ/m²

AKROMID®

Preliminary

NEXT U28 ICF 20 1 black (8690)

PA11 CF20

AKROMID® NEXT U28 ICF 20 1 black (8690) is a Polyamide 11 reinforced with 20% carbon fiber. The PA 11 is made from castor seed oil (bio-based content > 92%). The compound's low density as well as excellent ductility even at lower temperatures combine

Modulus

9.300MPa

Strength

110MPa

Impact

60kJ/m²

AKROMID®

B3 ICF 20 black (5103)

PA6 CF20

AKROMID® B3 ICF 20 black (5103) is a high performance Polyamide 6 with 20% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Thanks

Modulus

13.500MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID®

A3 ICF 15 black (5056)

PA66 CF15

AKROMID® A3 ICF 15 black (5056) is a high-performance Polyamide 6.6 with 15% carbon fiber reinforcement, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6.6, it provides an optimized strength-to-weight ratio. Than

Modulus

12.000MPa

Strength

170MPa

Impact

45kJ/m²

AKROMID®

A3 ICF 20 black (5102)

PA66 CF20

AKROMID® A3 ICF 20 black (5102) is a high-performance Polyamide 6.6 with 20% carbon fiber reinforcement, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6.6, it provides an optimized strength-to-weight ratio. Than

Modulus

16.000MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY®

PA ICF 20 black (5268)

PA66 + PA6I/6T CF20

AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

17.000MPa

Strength

200MPa

Impact

45kJ/m²

AKROTEK®

PK-VM ICF 15 black (6074)

PK CF15

AKROTEK® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

Modulus

9.000MPa

Strength

90MPa

Impact

30kJ/m²

AKROMID®

B3 ICF 20 LF black (6695)

PA6 CF20

AKROMID® B3 ICF 20 LF black (6695) is a high performance Polyamide 6 with 20% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Due

Modulus

15.000MPa

Strength

175MPa

Impact

50kJ/m²

AKROMID®

Preliminary

T5 ICF 20 black (6773)

PPA CF20

AKROMID® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties.

Modulus

18.000MPa

Strength

222MPa

Impact

37kJ/m²