PRECITE^®

Preliminary

P3 ICF 30 black (6948)PBT CF 30

PRECITE® P3 ICF 30 black (6948) is a medium viscous polybutylene terephthalate (PBT) with 30% recycled carbon fiber. Despite lower density compared to PBT with glass fiber reinforcement, the product has very high strength and toughness as well as high dimensional stability. The good tribological properties and improved surface finish make it the material of choice for precision components in the automotive, mechanical engineering, E&E and household goods industries.

Features

surface modified

recycled content

reduced density

tribological modified

3D printing / additive manufacturing

E&E

Sports & leisure

lightweight construction

Properties

Modulus

23.500MPa

Strength

175MPa

Impact

50kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

23500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

175 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

2,1 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

32500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

300 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

50 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

7 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

215 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

225 °C

Flammability

UL 94

0,8 mm Wall thickness

HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness

725 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General Properties

Density

ISO 1183

23°C

1,41 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

0,1 - 0,3 %

Water absorption

ISO 62

23°C, saturated

0,4 %

Molding shrinkage

ISO 294-4

flow

transverse

0,2 - 0,4 %

0,6 - 0,8 %

Electrical Properties

Surface resistivity

IEC 62631-3-2

d.a.m.

10³ Ω

Rheological Properties

MVR

ISO 1133

250°C/2,16kg

10 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.