AKROMID®

Preliminary

T5 ICF 20 black (6773)PPA CF20

AKROMID® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties.

Features

reduced density
lightweight construction
reused content

Properties

Modulus

18.000MPa

Strength

222MPa

Impact

37kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
18000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
222 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
1,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
37 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
325 °C

General Properties

Density

ISO 1183

23°C
1,28 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Surface resistivity

IEC 62631-3-2

d.a.m.
105 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B3 ICF 20 black (5103)

PA6 CF20

AKROMID® B3 ICF 20 black (5103) is a high performance Polyamide 6 with 20% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Thanks

Modulus

13.500MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID®

A3 ICF 15 black (5056)

PA66 CF15

AKROMID® A3 ICF 15 black (5056) is a high-performance Polyamide 6.6 with 15% carbon fiber reinforcement, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6.6, it provides an optimized strength-to-weight ratio. Than

Modulus

12.000MPa

Strength

170MPa

Impact

45kJ/m²

AKROMID®

A3 ICF 20 black (5102)

PA66 CF20

AKROMID® A3 ICF 20 black (5102) is a high-performance Polyamide 6.6 with 20% carbon fiber reinforcement, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6.6, it provides an optimized strength-to-weight ratio. Than

Modulus

16.000MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY®

PA ICF 20 black (5268)

PA66 + PA6I/6T CF20

AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

17.000MPa

Strength

200MPa

Impact

45kJ/m²

AKROMID®

B3 ICF 20 LF black (6695)

PA6 CF20

AKROMID® B3 ICF 20 LF black (6695) is a high performance Polyamide 6 with 20% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Due

Modulus

15.000MPa

Strength

175MPa

Impact

50kJ/m²

PRECITE®

P3 ICF 20 black (6947)

PBT CF20

PRECITE® P3 ICF 20 black (6947) is a PBT reinforced with 20% carbon fiber with excellent dimensional stability. Thanks to its low moisture absorption, PRECITE® achieves consistent mechanical and electrical properties, even under changing climatic co

Modulus

16.000MPa

Strength

150MPa

Impact

50kJ/m²

PRECITE®

Preliminary

E ICF 20 black (7428)

PET CF20

PRECITE® E ICF 20 black (7428) is a medium viscosity polyethylene terephthalate (PET) with 20% carbon fiber. Despite lower density compared to PET with glass fiber reinforcement, the product has very high strength and toughness as well as high dimens

Modulus

17.000MPa

Strength

180MPa

Impact

41kJ/m²

AKROMID®

B3 ICF 15 black (5026)

PA6 CF15

AKROMID® B3 ICF 15 black (5026) is a high performance Polyamide 6 with 15% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Thanks

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

PRECITE®

Preliminary

P3 ICF 15 black (7720)

PBT CF15

PRECITE® P3 ICF 15 black (7720) is a medium viscous polybutylene terephthalate (PBT) with 15% carbon fiber. Despite lower density compared to PBT with glass fiber reinforcement, the product has a medium strength and toughness as well as high dimensio

Modulus

12.500MPa

Strength

135MPa

Impact

50kJ/m²

AKROMID®

Preliminary

T5 ICF 30 black (6410)

PPA CF30

AKROMID® T5 ICF 30 black (6410) is a 30% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties.

Modulus

27.000MPa

Strength

260MPa

Impact

45kJ/m²

PRECITE®

Preliminary

E ICF 15 black (7427)

PET CF15

PRECITE® E ICF 15 black (7427) is a medium viscosity polyethylene terephthalate (PET) with 15% carbon fiber. Despite lower density compared to PET with glass fiber reinforcement, the product has very high strength and toughness as well as high dimens

Modulus

13.000MPa

Strength

160MPa

Impact

25kJ/m²

AKROTEK®

PK-VM ICF 15 black (6074)

PK CF15

AKROTEK® PK-VM ICF 15 black (6074) is a 15% carbon fibre reinforced polyketon with good sliding properties.

Modulus

9.000MPa

Strength

90MPa

Impact

30kJ/m²