AKROMID®

Preliminary

T5 ICF 30 black (6410)PPA CF30

AKROMID® T5 ICF 30 black (6410) is a 30% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties.

Features

reduced density
lightweight construction
reused content

Properties

Modulus

27.000MPa

Strength

260MPa

Impact

45kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
27000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
260 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
1,2 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
25000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
390 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
1,7 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
6 kJ/m²
6 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
280 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
325 °C

General Properties

Density

ISO 1183

23°C
1,34 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Surface resistivity

IEC 62631-3-2

d.a.m.
< 103 Ω

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
120 mm
260 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

A3 ICF 30 black (5021)

PA66 CF30

AKROMID® A3 ICF 30 black (5021) is a high-performance Polyamide 6.6 with 30% carbon fiber reinforcement, offering exceptional stiffness and flexural strength. Compared to glass fiber-reinforced PA 6.6, it provides an optimized strength-to-weight rati

Modulus

24.000MPa

Strength

240MPa

Impact

55kJ/m²

AKROMID®

B3 ICF 30 black (5119)

PA6 CF30

AKROMID® B3 ICF 30 black (5119) is a high performance Polyamide 6 with 30% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Thanks

Modulus

23.000MPa

Strength

200MPa

Impact

55kJ/m²

AKROMID®

Preliminary

T5 ICF 20 black (6773)

PPA CF20

AKROMID® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties.

Modulus

18.000MPa

Strength

222MPa

Impact

37kJ/m²

PRECITE®

Preliminary

P3 ICF 30 black (6948)

PBT CF30

PRECITE® P3 ICF 30 black (6948) is a PBT reinforced with 30% carbon fiber with excellent dimensional stability. Thanks to its low moisture absorption, PRECITE® achieves consistent mechanical and electrical properties, even under changing climatic co

Modulus

23.500MPa

Strength

175MPa

Impact

50kJ/m²

PRECITE®

E ICF 30 black (7429)

PET CF30

PRECITE® E ICF 30 black (7429) is medium viscosity polyethylene terephthalate (PET) with 30% carbon fiber. Despite lower density compared to PET with glass fiber reinforcement, the product has very high strength and toughness as well as high dimensio

Modulus

26.000MPa

Strength

220MPa

Impact

44kJ/m²

AKROMID®

B3 ICF 30 AM black (7451)

PA6 CF30

AKROMID® B3 ICF 30 AM black (7451) is a high performance Polyamide 6 with 30% carbon fiber reinforcement and optimized viscosity for 3D printing, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an o

Modulus

20.000MPa

Strength

190MPa

Impact

45kJ/m²

AKROMID®

Preliminary

T9 ICF 30 1 black (7908)

PPA CF30

AKROMID® T9 ICF 30 1 black (7908) is a 30% carbon fibre polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to

Modulus

26.000MPa

Strength

235MPa

Impact

40kJ/m²

AKROMID®

A3 ICF 20 black (5102)

PA66 CF20

AKROMID® A3 ICF 20 black (5102) is a high-performance Polyamide 6.6 with 20% carbon fiber reinforcement, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6.6, it provides an optimized strength-to-weight ratio. Than

Modulus

16.000MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY®

PA ICF 30 black (5269)

PA66+PA6I/6T CF30

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

25.000MPa

Strength

220MPa

Impact

50kJ/m²

AKROMID®

B3 ICF 10 1 black (6194)

PA6 CF10

AKROMID® B3 ICF 10 1 black (6194) is a heat stabilised Polyamide 6 with 10% carbon fiber reinforcement, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Thanks

Modulus

8.500MPa

Strength

125MPa

Impact

45kJ/m²

AKROMID®

A3 ICF 30 5 black (6495)

PA66 CF30

AKROMID® A3 ICF 30 5 black (6495) is a high-performance Polyamide 6.6 with 30% carbon fiber reinforcement which is high heat stabilised, offering exceptional stiffness and flexural strength. Compared to glass fiber-reinforced PA 6.6, it provides an o

Modulus

23.000MPa

Strength

235MPa

Impact

50kJ/m²

AKROMID®

B3 ICF 20 LF black (6695)

PA6 CF20

AKROMID® B3 ICF 20 LF black (6695) is a high performance Polyamide 6 with 20% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Due

Modulus

15.000MPa

Strength

175MPa

Impact

50kJ/m²