AKROLOY®

UL

PARA GF 60 HU black (8519)PARA GF60

AKROLOY® PARA GF 60 HU black (8519) is a 60% glass fibre reinforced polyarylamid with very high stiffness and strength, even in conditioned state owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys. The material is listed at UL in all colors.

Features

reduced moisture
easy flow
metal substitution

Regulatory

ul

Properties

Modulus

24.000MPa

Strength

310MPa

Impact

80kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
24000 MPa
24000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
310 MPa
280 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,0 %
2,0 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
23500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
400 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
80 kJ/m²
85 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/C

ISO 75

8 MPa
205 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
238 °C

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
HB Class
HB Class
HB Class

HWI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
4 PLC
2 PLC
2 PLC

HAI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,76 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,2 %
0,2 - 0,4 %

Electrical Properties


Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.