AKROLOY®

UL

PARA GF 40 HU natural (8512)PARA GF40

AKROLOY® PARA GF 40 HU natural (8512) is a 40% glass fibre reinforced polyarylamid with very high stiffness and strength, even in conditioned state it impresses with very high stiffness and strength owing to its lower moisture uptake. Furthermore, the material shows very good flowability and surface properties. It is perfectly suitable for parts where dimensional stabilitiy is required. Besides, it can be used as an alternative for aluminium and zinc diecast alloys. The material is listed at UL in all colors.

Features

reduced moisture
easy flow
metal substitution

Regulatory

ul

Properties

Modulus

15.000MPa

Strength

255MPa

Impact

Na

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
15000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
255 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,3 %

Thermal Properties


RTI electrical

UL 746B

0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
65 °C
65 °C
65 °C

RTI impact

UL 746B

0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
65 °C
65 °C
65 °C

RTI strength

UL 746B

0,8mm Wall thickness
1,6mm Wall thickness
3,2mm Wall thickness
65 °C
65 °C
65 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
238 °C

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
HB Class
HB Class
HB Class

HWI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
4 PLC
2 PLC
2 PLC

HAI

UL 746A

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Electrical Properties


Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.