AKROMID®

Preliminary

B25 GF 30 1 FR natural (8954)PA6 GF30 FR(40)

AKROMID® B25 GF 30 1 FR natural (8954) is a flame-retardant, heat-stabilised, 30% glass fibre-reinforced PA6. The material is based on a flame-retardant system that is free of red phosphorus, halogens, melamine, zink borate and PFAS. It achieves a V0 classification from a thickness of 0.4 mm and complies with IEC 60335 GWEPT requirements. This product is designed for high flowability for thin walled parts. Suitable applications are in the appliance industry, E&E market and E-mobility sector. For applications with component thicknesses from 1.6 mm, we recommend our AKROMID® B28 GF 30 9 FR natural (8069).

Features

heat stabilised 130
flame retardant
easy flow
process improved
E&E
household appliances
E-Mobility

Properties

Modulus

11.000MPa

Strength

145MPa

Impact

65kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
7400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
145 MPa
95 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,0 %
5,1 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
11300 MPa
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
230 MPa
155 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3 %
5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
40°C | d.a.m.
-
65 kJ/m²
70 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
40°C | d.a.m.
-
11 kJ/m²
15 kJ/m²
10 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
800 °C
800 °C
800 °C
775 °C

General Properties

Density

ISO 1183

23°C
1,4 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,6-1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.