AKROTEK®

Preliminary

PK-VM GF 30 black (86550)PK GF30

AKROTEK® PK-VM GF 30 black (86550) is a 30% glass fiber reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for the use in applications that carry cooling water. The material can be laser marked and has an excellent surface and demouling performance.

Features

hydrolysis / chemically stabilised
E-Mobility

Properties

Modulus

8.500MPa

Strength

130MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
130 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
11 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

General Properties

Density

ISO 1183

23°C
1,48 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,6 - 0,7 %

Water absorption

ISO 62

23°C, saturated
1,6 - 1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,8 - 1,0 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROTEK®

PK-VM GF 30 black (8655)

PK GF30

AKROTEK® PK-VM GF 30 black (8655) is a 30% glass fiber reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for the use in applications that carry cooling water. The material can b

Modulus

8.500MPa

Strength

130MPa

Impact

70kJ/m²

AKROTEK®

UL
Preliminary

PK-VM GF 30 FR black (8604)

PK GF30 FR(44)

AKROTEK® PK-VM GF 30 FR black (8604) is a 30% glass fibre reinforced, flame retardant and process improved Polyketone compound, colored in black. The flame retardant system is free of red phosphorous, PFAS, melamine, halogens and antimony trioxide. D

Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

AKROTEK®

UL
Preliminary

PK-VM GF 30 HU black (9175)

PK GF30

AKROTEK® PK-VM GF 30 HU black (9175) is a 30% glass fiber reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for the use in applications that carry cooling water. The material c

Modulus

8.500MPa

Strength

130MPa

Impact

70kJ/m²

AKROTEK®

UL

PK-VM GF 30 FR orange (8537)

PK GF30 FR(44)

AKROTEK® PK-VM GF 30 FR orange (8537) is a 30% glass fibre reinforced, flame retardant and process improved Polyketone compound, colored in orange similar to RAL 2003. The flame retardant system is free of red phosphorous, PFAS, melamine, halogens an

Modulus

8.600MPa

Strength

115MPa

Impact

62kJ/m²

AKROTEK®

PK-VM GF 30 natural (8661)

PK GF30

AKROTEK® PK-VM GF 30 natural (8661) is a 30% glass fiber reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for the use in applications that carry cooling water. This type was d

Modulus

8.300MPa

Strength

144MPa

Impact

76kJ/m²

AKROTEK®

UL
Preliminary

PK-VM GF 30 FR natural (8448)

PK GF30 FR(44)

AKROTEK® PK-VM GF 30 FR natural (8448) is a 30% glass fibre reinforced, flame retardant and process improved Polyketone compound. The flame retardant system is free of red phosphorous, PFAS, melamine, halogens and antimony trioxide. Due to its good c

Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

AKROTEK®

UL

PK-VM GF 30 7 HU black (8695)

PK GF30

AKROTEK® PK-VM GF 30 7 HU black (8695) is a 30% glass fibre reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for the use in applications that carry cooling water. The PK-VM GF

Modulus

8.000MPa

Strength

130MPa

Impact

65kJ/m²

AKROMID®

UL
Preliminary

T91 GF 30 FR black (8184)

PPA GF30 FR(44)

AKROMID® T91 GF 30 FR black (8184) is an easy flow, flame retardant and 30% glass fiber reinforced Polyamide 9T with high stiffness and strength. This material is based on the latest flame retardant technology, that is free of red phosphorous, melami

Modulus

11.000MPa

Strength

140MPa

Impact

40kJ/m²

AKROTEK®

Preliminary

PK-VM GF 30 8 black (9153)

PK GF30

AKROTEK® PK-VM GF 30 8 black (9153) is a 30% glass fibre reinforced polyketone with high stiffness and strength. PK is characterized by its outstanding media resistance, which qualifies it to be used for components that are in contact with chemicals.

Modulus

8.100MPa

Strength

130MPa

Impact

65kJ/m²

AKROTEK®

UL
Preliminary

PK-VM GF 15 HU black (9176)

PK GF15

AKROTEK® PK-VM GF 15 HU black (9176) is a 15% glass fiber reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for the use in applications that carry cooling water. The material

Modulus

4.500MPa

Strength

90MPa

Impact

50kJ/m²

AKROMID®

A3 GF 30 4 6 black (13690)

PA66 GF30

AKROMID® A3 GF 30 4 6 black (13690) is a 30% glass fiber reinforced, high heat stabilised, hydrolysis- and chemical resistant polyamide 6.6 with high stiffness and strength. It is the official DPPD-free successor of formulation 1369. The material can

Modulus

10.000MPa

Strength

190MPa

Impact

85kJ/m²

AKROMID®

UL

A3 GF 30 FR black (7751)

PA66 GF30 FR(44)

AKROMID® A3 GF 30 FR black (7751) is a 30 % glass fibre reinforced, flame-retardant and heat-stabilized PA6.6, colored in black similar to RAL 9005. The material is listed by UL in all-colors. It is based on a flame retardant system that is free from

Modulus

10.500MPa

Strength

150MPa

Impact

67kJ/m²