AKROMID®

A28 GF 35 6 black (7278)PA66 GF35

AKROMID® A28 GF 35 6 black (7278) is a 35% glass fiber reinforced, easy-flowing, inorganically highly heat-stabilized polyamide 6.6. The material is characterized by easy processability due to its very good flowability. Its high rigidity and strength make it the material of choice for technical components in mechanical engineering and the automotive industry. For electrical insulation components, AKROMID® materials containing electrically neutral Type 1 stabilizers are recommended.

Features

laser markable
easy flow

Properties

Modulus

11.200MPa

Strength

205MPa

Impact

80kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11200 MPa
7300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
205 MPa
130 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
10800 MPa
6900 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
300 MPa
210 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
80 kJ/m²
90 kJ/m²
60 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
12 kJ/m²
17 kJ/m²
10 kJ/m²
10 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,4 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,8 - 2,0 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,65 - 0,85 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

A28 GF 50 1 GIT black (5029)

PA66 GF50

AKROMID® A28 GF 50 1 GIT black (5029) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6.6. It is characterised by very high stiffness and strength and shows an excellent surface. Furthermore, the material is designed for gas

Modulus

17.500MPa

Strength

270MPa

Impact

100kJ/m²

AKROMID®

Preliminary

B25 GF 50 LA black (8280)

PA6 GF50

AKROMID® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

Modulus

15.500MPa

Strength

235MPa

Impact

100kJ/m²

AKROMID®

UL

A3 GF 35 1 HU black (8417)

PA66 GF35

AKROMID® A3 GF 35 1 HU black (8417) is a 35% glass fibre reinforced, heat ageing resistant polyamide 6.6 with high rigidity and strength. The material is colored in black and has a very good flowability. This UL94 HB listed grade is suitable for tech

Modulus

12.000MPa

Strength

215MPa

Impact

75kJ/m²

AKROMID®

Preliminary

A28 GF 33 1 LA black (6686)

PA66 GF33

AKROMID® A28 GF 33 1 LA black (6686) is a 33% glass fiber reinforced, easy flowing polyamide 6.6. The material is characterised by good processability due to its very good flowability. Owing to its high stiffness and strength, it is perfectly suitabl

Modulus

11.000MPa

Strength

205MPa

Impact

85kJ/m²

AKROLOY®

Preliminary

PARA GF 35 1 FR black (9023)

PARA GF35 FR(44)

AKROLOY® PARA GF 35 1 FR black (9023) is a 35% glass fibre reinforced, flame-retardant and heat-stabilized polyarylamide with very high rigidity and strength. The material is based on a flame retardant system that is free of red phosphorus, PFAS, zin

Modulus

14.500MPa

Strength

190MPa

Impact

55kJ/m²

AKROLOY®

Preliminary

NEXT PARA GF 35 1 FR black (9023BMBCI)

PARA GF35 FR(44)

AKROLOY® NEXT PARA GF 35 1 FR black (9023BMBCI) is a 35% glass fibre reinforced, flame-retardant and heat-stabilized polyarylamide with very high rigidity and strength. The material is based on a flame retardant system that is free of red phosphorus,

Modulus

14.500MPa

Strength

190MPa

Impact

55kJ/m²

AKROMID®

A3 GF 35 3 black (1802)

PA66 GF35

AKROMID® A3 GF 35 3 black (1802) is a 35% glass fiber reinforced polyamide 6.6. It is characterised by a high stiffness and strength. Furthermore, the material is nucleated. It is perfectly suitable for technical parts in industrial engineering and i

Modulus

11.500MPa

Strength

180MPa

Impact

50kJ/m²

AKROMID®

A3 GF 40 1 black (2386)

PA66 GF40

AKROMID® A3 GF 40 1 black (2386) is a 40% glass fiber reinforced polyamide 6.6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial

Modulus

13.100MPa

Strength

225MPa

Impact

100kJ/m²

AKROMID®

A3 GF 35 1 black (2269)

PA66 GF35

AKROMID® A3 GF 35 1 black (2269) is a 35% glass fiber reinforced polyamide 6.6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engi

Modulus

11.600MPa

Strength

215MPa

Impact

92kJ/m²

AKROMID®

A3 GF 50 1 black (2387)

PA66 GF50

AKROMID® A3 GF 50 1 black (2387) is a 50% glass fiber reinforced polyamide 6.6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID®

A3 GF 40 1 L black (4671)

PA66+PP GF40

AKROMID® A3 GF 40 1 L black (4671) is a PA6.6-PP-blend with reduced density compared to standard PA66 GF 30. With 30% glass fibre reinforcement, the material is suitable for components with high strength and stiffness where cost and weight reduction

Modulus

11.800MPa

Strength

170MPa

Impact

80kJ/m²

AKROMID®

B28 GF 50 1 GIT black (4732)

PA6 GF50

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

Modulus

16.700MPa

Strength

235MPa

Impact

105kJ/m²