PRECITE®

Preliminary

K GF 50 ECO black (8270)

PBT-PET- GF 50

PRECITE® K GF 50 ECO black (8270) is a 50% glass fibre reinforced PBT/PET blend with high strength and improved surface finish. Due to its low moisture absorption, this material is particularly suitable for precision parts in the automotive, E&E or appliances industries. The formulations of the sustainable ECO products are partly based on regenerated post-consumer feedstock and thus contribute to reducing the consumption of valuable raw materials.

Features

recycled content
surface modified
E&E
Sports & leisure

Properties

Modulus

17.000MPa

Strength

180MPa

Impact

66kJ/m²

Sustainability


Recycled content

20 %

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
17000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
180 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
1,8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
66 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
11 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
250 °C

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
HB Class

General properties


Density

ISO 1183

23°C
1,74 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,1 - 0,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.