AKROMID®

Preliminary

B3 GF 35 ECO black (9173)PA6 GF35

AKROMID® B3 GF 35 ECO black (9173) is a 35% glass fibre-reinforced, heat-stabilised polyamide 6 with a basic laser markability. The formulation of this ECO product is partly based on post-consumer recycled feedstock. The material is suitable for technical components with demands for high stiffness and strength in mechanical engineering and automotive industry.

Features

heat stabilised 130
laser markable
recycled content

Properties

Modulus

10.800MPa

Strength

165MPa

Impact

75kJ/m²

Sustainability Aspects

Recycled content

ISO 14021

Post-consumer (PCR)
> 30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
165 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
75 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
11 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,42 g/cm³

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

UL
Preliminary

B3 GF 35 1 HU black (8982)

PA6 GF35

AKROMID® B3 GF 35 1 black (8982) is a 30% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engine

Modulus

11.500MPa

Strength

195MPa

Impact

86kJ/m²

AKROMID®

Preliminary

B3 GF 15 ECO black (9171)

PA6 GF15

AKROMID® B3 GF 15 ECO black (9171) is a 15% glass fibre-reinforced, heat-stabilised polyamide 6 with a basic laser markability. The formulation of this ECO product is partly based on post-consumer recycled feedstock. The material is suitable for tec

Modulus

6.300MPa

Strength

120MPa

Impact

35kJ/m²

AKROMID®

Preliminary

B3 GF 30 ECO black (9172)

PA6 GF30

AKROMID® B3 GF 30 ECO black (9172) is a 30% glass fibre-reinforced, heat-stabilised polyamide 6 with a basic laser markability. The formulation of this ECO product is partly based on post-consumer recycled feedstock. The material is suitable for tech

Modulus

10.000MPa

Strength

160MPa

Impact

60kJ/m²

AKROMID®

B3 GF 40 1 black (2487)

PA6 GF40

AKROMID® B3 GF 40 1 black (2487) is a 40% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength.

Modulus

12.800MPa

Strength

205MPa

Impact

100kJ/m²

AKROMID®

B3 GF 50 1 black (2488)

PA6 GF50

AKROMID® B3 GF 50 1 black (2488) is a 50% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial e

Modulus

17.000MPa

Strength

215MPa

Impact

90kJ/m²

AKROMID®

B3 GF 45 1 black (3851)

PA6 GF45

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID®

B28 GF 50 1 GIT black (4732)

PA6 GF50

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

Modulus

16.700MPa

Strength

235MPa

Impact

105kJ/m²

AKROMID®

B28 GF 30 1 black (4962)

PA6 GF30

AKROMID® B28 GF 30 1 black (4962) is a 30% glass fiber reinforced, easy flowing polyamide 6. It is characterised by a high stiffness and strength. The material is therefore perfectly suitable for technical parts not only in industrial engineering and

Modulus

9.500MPa

Strength

170MPa

Impact

75kJ/m²

AKROMID®

B3 GF 50 1 black (20008)

PA6 GF50

AKROMID® B3 GF 50 black (20008) is a 50% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial en

Modulus

17.000MPa

Strength

210MPa

Impact

80kJ/m²

AKROMID®

B28 GF 35 FR EN black (7484)

PA6 GF35 FR(44)

AKROMID® B28 GF 35 FR EN black (7484) is a flame retardant PA6 with 35% glass fibres. The flame retardant system is free of red phosphorus and halogens, leading to optimised electrical properties for e-mobility applications. Due to formulation and p

Modulus

12.600MPa

Strength

152MPa

Impact

70kJ/m²

AKROMID®

B3 CGM 15/20 1 LA black (8058)

PA6 (CF15+GF20)

AKROMID® B3 CGM 15/20 1 LA black (8058) is a 15% carbon fibre reinforced, 20% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength. Furthermore, the material impresses with its good laser marking properties as well as

Modulus

16.500MPa

Strength

185MPa

Impact

60kJ/m²

AKROMID®

UL

B28 GF 35 9 FR black (8189)

PA6 GF35 FR(44)

AKROMID® B28 GF 35 9 FR black (8189) is a flame retardant PA6 with 35% glass fibres. The flame retardant system is free of red phosphorus and halogens, leading to optimised electrical properties for e-mobility applications. This grade is UL listed wi

Modulus

12.600MPa

Strength

160MPa

Impact

70kJ/m²