AKROMIDĀ®
T5 GF 50 6 black (8000)
PPA GF50
Standard Grade with good surface quality. AKROMIDĀ® T5 GF 50 6 black (8000) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up
18.500MPa
260MPa
65kJ/mĀ²
Standard Grade with good surface quality. AKROMIDĀ® T5 GF 50 6 black (8000) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up
AKROMIDĀ®
A3 GF 30 HU natural (6661)
PA66 GF30
AKROMIDĀ® A3 GF 30 HU natural (6661) - PA 6.6 30% glass fiber reinforced, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and in the automotive industry
10.500MPa
200MPa
75kJ/mĀ²
AKROMIDĀ® A3 GF 30 HU natural (6661) - PA 6.6 30% glass fiber reinforced, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and in the automotive industry
AKROMIDĀ®
C3 GF 25 1 FR orange (7854)
PA66+PA6 GF25 FR(40)
AKROMIDĀ® C3 GF 25 1 FR orange (7854) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, RAL 2003, automotive, E&E.
9.000MPa
126MPa
61kJ/mĀ²
AKROMIDĀ® C3 GF 25 1 FR orange (7854) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, RAL 2003, automotive, E&E.
AKROTEKĀ®
PK-VM GF 30 FR orange (8537)
PK GF30 FR(40)
AKROTEKĀ® PK-VM GF 30 FR orange (8537) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.
8.600MPa
125MPa
70kJ/mĀ²
AKROTEKĀ® PK-VM GF 30 FR orange (8537) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.
AKROTEKĀ®
PK-VM GF 30 black (8655)
PK GF30
AKROTEKĀ® PK-VM GF 30 black (8655) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance
8.500MPa
130MPa
70kJ/mĀ²
AKROTEKĀ® PK-VM GF 30 black (8655) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance
AKROMIDĀ®
B28 GF 30 9 FR orange (8645)
PA6 GF30 FR(40)
AKROMIDĀ® B28 GF 30 9 FR orange (8645) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.
10.200MPa
138MPa
70kJ/mĀ²
AKROMIDĀ® B28 GF 30 9 FR orange (8645) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.
AKROTEKĀ®
PK-VM GF 15 black (8686)
PK GF15
AKROTEKĀ® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance
4.500MPa
90MPa
50kJ/mĀ²
AKROTEKĀ® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance
AKROMIDĀ®
C3 GF 25 1 FR black (7246)PA66+PA6 GF25 FR(40)
AKROMIDĀ® C3 GF 25 1 FR black (7246) is a 25 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend, colored in black. Listed to UL 94 in black V0 @ 0,4 mm and all-colours V0 @ 0,8mm, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved. This grade is also suitable for applications with high strength requirements in the automotive and E&E markets.
Features
Regulatory
Properties
9.100MPa
137MPa
66kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
RTI electrical
UL 746B
RTI impact
UL 746B
RTI strength
UL 746B
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Ball pressure test
IEC 60695-10-2
Temperature index for 50% loss of tensile strength
IEC 60216
Flammability
Burning rate
UL 94
Burning rate 5V
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
HWI
UL 746A
HAI
UL 746A
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Comparative tracking index
IEC 60112
Dielectric strength
IEC 60243
Inclined-Plane Tracking, IPT
ASTM D2303-13
High voltage arc tracking rate (HVTR)
UL 746A
High Volt, Low Current Arc Resistance
ASTM D495
Rheological Properties
Flowability
AKRO
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.