AKROMID®

UL
Preliminary

C3 GF 25 1 FR orange (7854)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR orange (7854) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, RAL 2003, automotive, E&E.


Modulus

9.000MPa

Strength

126MPa

Impact

61kJ/m²

AKROMID® C3 GF 25 1 FR orange (7854) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, RAL 2003, automotive, E&E.

AKROMID®

UL

A3 GF 30 HU natural (6661)

PA66 GF30

AKROMID® A3 GF 30 HU natural (6661) - PA 6.6 30% glass fiber reinforced, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and in the automotive industry


Modulus

10.500MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 HU natural (6661) - PA 6.6 30% glass fiber reinforced, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and in the automotive industry

AKROMID®

Preliminary

T5 GF 50 6 black (8000)

PPA GF50

Standard Grade with good surface quality. AKROMID® T5 GF 50 6 black (8000) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up


Modulus

18.500MPa

Strength

260MPa

Impact

65kJ/m²

Standard Grade with good surface quality. AKROMID® T5 GF 50 6 black (8000) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up

AKROMID®

UL
Preliminary

B28 GF 30 9 FR orange (8645)

PA6 GF30 FR(40)

AKROMID® B28 GF 30 9 FR orange (8645) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.


Modulus

10.200MPa

Strength

138MPa

Impact

70kJ/m²

AKROMID® B28 GF 30 9 FR orange (8645) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

AKROTEK®

UL
Preliminary

PK-VM GF 30 FR orange (8537)

PK GF30 FR(40)

AKROTEK® PK-VM GF 30 FR orange (8537) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.


Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 30 FR orange (8537) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.

AKROTEK®

Preliminary

PK-VM GF 15 black (8686)

PK GF15

AKROTEK® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance


Modulus

4.500MPa

Strength

90MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEK®

PK-VM GF 30 black (8655)

PK GF30

AKROTEK® PK-VM GF 30 black (8655) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance


Modulus

8.500MPa

Strength

130MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 30 black (8655) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

123481

AKROMID®

A3 GM 25/15 1 black (7003)PA66 (GF25+GB15)

AKROMID® A3 GM 25/15 1 black (7003) is a 25% glass fiber and 15% glass beads reinforced, heat stabilised PA 6.6. The material impresses with a good surface appearance and low warpage and is therefore perfectly suitable for technical demanding components in the mechanical engineering and automotive industry.

Features

heat stabilised 130
low warpage

Properties

Modulus

10.000MPa

Strength

180MPa

Impact

70kJ/m²

Sustainability


Recycled content

15 %

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10000 MPa
7000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
180 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
8 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
10200 MPa
7500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
275 MPa
205 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,4 %
5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
70 kJ/m²
80 kJ/m²
57 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
10 kJ/m²
8 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,46 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more