AKROMIDĀ®
T5 GF 50 6 black (8000)
PPA GF50
Standard Grade with good surface quality. AKROMIDĀ® T5 GF 50 6 black (8000) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up
18.500MPa
260MPa
65kJ/mĀ²
Standard Grade with good surface quality. AKROMIDĀ® T5 GF 50 6 black (8000) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up
AKROMIDĀ®
A3 GF 30 HU natural (6661)
PA66 GF30
AKROMIDĀ® A3 GF 30 HU natural (6661) - PA 6.6 30% glass fiber reinforced, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and in the automotive industry
10.500MPa
200MPa
75kJ/mĀ²
AKROMIDĀ® A3 GF 30 HU natural (6661) - PA 6.6 30% glass fiber reinforced, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and in the automotive industry
AKROTEKĀ®
PK-VM GF 30 FR orange (8537)
PK GF30 FR(40)
AKROTEKĀ® PK-VM GF 30 FR orange (8537) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.
8.600MPa
125MPa
70kJ/mĀ²
AKROTEKĀ® PK-VM GF 30 FR orange (8537) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.
AKROTEKĀ®
PK-VM GF 15 black (8686)
PK GF15
AKROTEKĀ® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance
4.500MPa
90MPa
50kJ/mĀ²
AKROTEKĀ® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance
AKROTEKĀ®
PK-VM GF 30 black (8655)
PK GF30
AKROTEKĀ® PK-VM GF 30 black (8655) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance
8.500MPa
130MPa
70kJ/mĀ²
AKROTEKĀ® PK-VM GF 30 black (8655) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance
AKROMIDĀ®
B28 GF 30 9 FR orange (8645)
PA6 GF30 FR(40)
AKROMIDĀ® B28 GF 30 9 FR orange (8645) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.
10.200MPa
138MPa
70kJ/mĀ²
AKROMIDĀ® B28 GF 30 9 FR orange (8645) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.
PRECITEĀ®
K GF 30 4 LA ECO black (8699)
PBT-PET- GF 30
PRECITEĀ® K GF 30 4 ECO black (8699) - PBT/PET blend, regenerated post-consumer PET, glass fibre, hydrolysis stabillised, high strength, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.
9.500MPa
120MPa
65kJ/mĀ²
PRECITEĀ® K GF 30 4 ECO black (8699) - PBT/PET blend, regenerated post-consumer PET, glass fibre, hydrolysis stabillised, high strength, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.
AKROMIDĀ®
A3 ICF 20 black (5102)PA66 CF20
AKROMIDĀ® A3 ICF 20 black (5102) is a high-performance Polyamide 6.6 with 20% carbon fiber reinforcement, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6.6, it provides an optimized strength-to-weight ratio. Thanks to its low density and high mechanical durability, this material is ideal for load-bearing components in the automotive industry, such as lightweight structural parts, as well as for sports and leisure applications, including high-stress sports equipment and technical components.
Features
Properties
16.000MPa
190MPa
50kJ/mĀ²
Sustainability
Recycled content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Thermal conductivity
DIN 52612
Flammability
Flammability
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General Properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Surface resistivity
IEC 62631-3-2
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.