AKROMID®

UL

A3 GF 30 HU natural (6661)

PA66 GF30

AKROMID® A3 GF 30 HU natural (6661) - PA 6.6 30% glass fiber reinforced, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and in the automotive industry


Modulus

10.500MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 HU natural (6661) - PA 6.6 30% glass fiber reinforced, heat stabilised, listed at UL in all colors, technical parts in industrial engineering and in the automotive industry

AKROMID®

Preliminary

T5 GF 50 6 black (8000)

PPA GF50

Standard Grade with good surface quality. AKROMID® T5 GF 50 6 black (8000) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up


Modulus

18.500MPa

Strength

260MPa

Impact

65kJ/m²

Standard Grade with good surface quality. AKROMID® T5 GF 50 6 black (8000) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up

AKROMID®

UL
Preliminary

C3 GF 25 1 FR orange (7854)

PA66/6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR orange (7854) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, RAL 2003, automotive, E&E.


Modulus

9.000MPa

Strength

126MPa

Impact

61kJ/m²

AKROMID® C3 GF 25 1 FR orange (7854) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, RAL 2003, automotive, E&E.

AKROTEK®

UL
Preliminary

PK-VM GF 30 FR orange (8537)

PK GF30 FR(40)

AKROTEK® PK-VM GF 30 FR orange (8537) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.


Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 30 FR orange (8537) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, orange RAL 2003, process improved, good dimensional stability. high voltage components, e-mobility.

AKROTEK®

PK-VM GF 30 black (8655)

PK GF30

AKROTEK® PK-VM GF 30 black (8655) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance


Modulus

8.500MPa

Strength

130MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 30 black (8655) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

AKROMID®

UL
Preliminary

B28 GF 30 9 FR orange (8645)

PA6 GF30 FR(40)

AKROMID® B28 GF 30 9 FR orange (8645) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.


Modulus

10.200MPa

Strength

138MPa

Impact

70kJ/m²

AKROMID® B28 GF 30 9 FR orange (8645) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

AKROTEK®

Preliminary

PK-VM GF 15 black (8686)

PK GF15

AKROTEK® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance


Modulus

4.500MPa

Strength

90MPa

Impact

50kJ/m²

AKROTEK® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance

123480

AKROMID®

B3 GF 30 1 black (2485)PA6 GF30

AKROMID® B3 GF 30 1 black (2485) is a 30% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry.

Features

heat stabilised 130

Properties

Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10300 MPa
6200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
185 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
270 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
75 kJ/m²
105 kJ/m²
70 kJ/m²
85 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
12 kJ/m²
18 kJ/m²
12 kJ/m²
12 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
150 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,19 10⁻⁴/K
1,09 10⁻⁴/K

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
> 650 °C
> 650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 - 2,3 %

Water absorption

ISO 62

23°C, saturated
6,3 - 6,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties


Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012
1010

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more