AKROMID®
A3 CGM 10/20 4 black (5870)
PA66 (CF10+GF20)
AKROMID® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity
14.500MPa
190MPa
65kJ/m²
AKROMID® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity
AKROMID®
B3 GF 30 6 black (20009)
PA6 GF30
AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
10.000MPa
180MPa
80kJ/m²
AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
A3 GF 30 8 HU natural (8102)
PA66 GF30
AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
10.500MPa
200MPa
75kJ/m²
AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
AKROMID®
B3 GF 40 black (6077)
PA6 GF40
AKROMID® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
13.000MPa
205MPa
110kJ/m²
AKROMID® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
AKROMID®
T9 GF 50 black (7601)
PPA GF50
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
17.000MPa
250MPa
95kJ/m²
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROLOY®
PARA GF 35 FR orange (8039)
PARA GF35 FR(40)
AKROLOY® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.
14.500MPa
190MPa
50kJ/m²
AKROLOY® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.
AKROMID®
A3 GF 30 8 HU black (8112)
PA66 GF30
AKROMID® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
10.500MPa
200MPa
75kJ/m²
AKROMID® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
AKROMID®
AKROMID® A3 GF 30 FR orange (7871) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors. This material is coloured similar RAL2003
Features
Regulatory
Properties
10.400MPa
140MPa
60kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 75
ISO 11357-3
UL 94
IEC 60695-2-12
IEC 60695-2-13
UL 746A
UL 746A
ISO 1183
ISO 1110
ISO 294-4
DIN EN IEC 62631-3-2
DIN EN 62631-3-2
IEC 60112
ASTM D3638
IEC 60243
ASTM D2303-13
UL 746A
ASTM D495
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.