PRECITE®

K ICF 20 4 ECO black (8795)PBT-PET- CF 20

PRECITE® K ICF 20 4 ECO black (8795) is a PBT/PET blend with 20% recycled carbon fiber hydrolysis stabilised. Despite lower density compared to PBT/PET blends with glass fiber reinforcement, the product has very high strength. The good tribological properties and improved surface finish make it the material of choice for precision components in automotive, mechanical engineering, E&E and household goods industries.

Features

hydrolysis / chemically stabilised
surface modified
recycled content

Properties

Modulus

13.600MPa

Strength

115MPa

Impact

50kJ/m²

Sustainability

Recycled content

28 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
13600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
115 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
50 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
9 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
250 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,32 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,1 - 0,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,7 - 0,9 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
103 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.