PETG GF 30 AM ECO natural (9107)PET-G (REC) GF30

AKROTEK® PETG GF 30 AM ECO natural (9107) is a 30% glass-fiber-reinforced, glycol-modified polyethylene terephthalate. The formulations of the sustainable ECO products are partly based on regenerated postindustrial feedstock saving valuable natural resources. It is characterized by medium stiffness and strength. The compound is optimized for pellet-based additive manufacturing (3D printing) and large format printing (LFAM). It is suitable for applications with operating temperatures up to 60 °C e.g. for mold making and fixtures. The material can be colored and is used in design applications and in the furniture industry.

Features

recycled content
3D printing / additive manufacturing
sustainable

Properties

Modulus

8.500MPa

Strength

105MPa

Impact

75kJ/m²

Sustainability

Recycled content

69 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
105 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
4 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
75 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
80 °C

Flammability

Flammability

UL 94

0,8 mm Wall thickness
HB Class

General Properties

Density

ISO 1183

23°C
1,49 g/cm³

Rheological Properties

MVR

ISO 1133

250°C/2,16kg
6 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

UL

NEXT S3 GF 30 1 HU natural (8824)

PA6.10 GF30

AKROMID® NEXT S3 GF 30 1 natural (8824) is a partially biobased and heat-stabilised PA6.10. With 30% glass fibre reinforcement, the material is suitable for household and industrial applications with high demands on strength and stiffness. This susta

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

AKROMID®

C28 GF 25 FRT natural (7332)

PA-Blend GF25 FR(44)

C28 GF 25 FRT natural (7332) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/m²

PRECITE®

P3 GF 30 natural (6850)

PBT GF30

PRECITE® P3 GF 30 natural (6850) is a 30% glass fiber reinforced PBT with excellent dimensional stability. Thanks to its low moisture absorption, PRECITE® achieves consistent mechanical and electrical properties, even under changing climatic conditio

Modulus

10.000MPa

Strength

145MPa

Impact

65kJ/m²

PRECITE®

Preliminary

P3 ICF 30 black (6948)

PBT CF30

PRECITE® P3 ICF 30 black (6948) is a PBT reinforced with 30% recycled carbon fiber with excellent dimensional stability. Thanks to its low moisture absorption, PRECITE® achieves consistent mechanical and electrical properties, even under changing cl

Modulus

23.500MPa

Strength

175MPa

Impact

50kJ/m²

AKROMID®

Preliminary

A3 GF 30 6 ECO black (8160)

PA66 GF30

AKROMID® A3 GF 30 6 ECO black (8160) is a 30% glass fibre-reinforced, inorganically heat-stabilised polyamide 6.6. The compound is suitable for technical components in mechanical engineering and the automotive industry with demands for high stiffness

Modulus

9.000MPa

Strength

150MPa

Impact

50kJ/m²

PRECITE®

Preliminary

E GF 30 ECO black (8271)

PET GF30

PRECITE® E GF 30 ECO black (8271) is a 30% glass fibre reinforced, medium viscous polyethylene terephthalate (PET) with very high stiffness and toughness as well as high chemical resistance. Due to its low moisture absorption, this material is partic

Modulus

10.500MPa

Strength

170MPa

Impact

45kJ/m²

PRECITE®

Preliminary

K GF 30 ECO black (8269)

PBT+PET GF30

PRECITE® K GF 30 ECO black (8269) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish. Due to its low moisture absorption, this material is particularly suitable for precision parts in the automotive, E&E or a

Modulus

10.000MPa

Strength

150MPa

Impact

70kJ/m²

PRECITE®

Preliminary

K GF 30 4 LA ECO black (8699)

PBT+PET GF30

PRECITE® K GF 30 4 ECO black (8699) is a 30% glass fibre reinforced, hydrolysis stabilised PBT/PET blend with high strength. Due to its low moisture absorption, this material is particularly suitable for precision parts in the automotive, E&E or appl

Modulus

9.500MPa

Strength

120MPa

Impact

65kJ/m²

AKROMID®

Preliminary

NEXT 5.6 3 GF 30 natural (8405)

PA56 GF30

AKROMID® NEXT 5.6 3 GF 30 natur (8405) is a HMD-free (hexamethylenediamine) alternative to PA 6.6. The partly bio-based material with 30% glass fibre is suitable for parts with high demands on stiffness and strength.

Modulus

9.500MPa

Strength

185MPa

Impact

66kJ/m²

PRECITE®

Preliminary

K GF 10 ECO black (8696)

PBT+PET GF10

PRECITE® K GF 10 ECO black (8696) is a 10% glass fibre reinforced PBT/PET blend with high strength and improved surface finish. Due to its low moisture absorption, this material is particularly suitable for precision parts in the automotive, E&E or a

Modulus

4.800MPa

Strength

100MPa

Impact

25kJ/m²

AKROMID®

UL

NEXT S3 GF 50 1 HU natural (8826)

PA6.10 GF50

AKROMID® NEXT S3 GF 50 1 natural (8826) is a partially biobased and heat-stabilised PA6.10. With 50% glass fibre reinforcement, the material is suitable for household and industrial applications with high demands on strength and stiffness. This susta

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID®

UL

NEXT C3 GF 30 1 FR natural (7207BMBCI)

PA66+PA6 GF30 FR(44)

AKROMID® NEXT C3 GF 30 1 FR natural (7207BMBCI) is a 30 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend. It is based on a halogen- and antimony trioxide-free flame retardant system that is also free of red phosphorus, zinc

Modulus

10.700MPa

Strength

150MPa

Impact

76kJ/m²