AKROMID®

B3 GF 30 AM natural (8962) PA6 GF30

AKROMID® B3 GF 30 AM natural (8962) is a 30% glass fiber reinforced polyamide 6 with high stiffness and good sliding properties as well as optimized viscosity. It is suitable for pellet-based large format additive manufacturing processes (LFAM, FGF) at fast production speeds. The natural-colored compounds can be colored with AF Color masterbatches.

Features

surface modified
low warpage
process improved
3D printing / additive manufacturing

Properties

Modulus

8.500MPa

Strength

145MPa

Impact

80kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
4 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
80 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
12 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

General Properties

Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 - 2,3 %

Water absorption

ISO 62

23°C, saturated
6,3 - 6,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

C28 GF 25 FRT natural (7332)

PA-Blend GF25 FR(44)

C28 GF 25 FRT natural (7332) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/m²

AKROMID®

B28 GF 30 9 natural (6614)

PA6 GF30

AKROMID® B28 GF 30 9 natural (6614) is a 30% glass fibre reinforced, easy flowing polyamide 6. The material is characterised by good surface properties due to its very good flowability. Furthermore, the material is easy to color. Owing to its high st

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID®

B3 GK 30 natural (2719)

PA6 GB30

AKROMID® B3 GK 30 natural (2719) is a PA 6 filled with 30% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the a

Modulus

4.400MPa

Strength

70MPa

Impact

30kJ/m²

AKROMID®

UL
Preliminary

B28 GM 15/15 1 FR natural (8861)

PA6 (GF15+GB15) FR(44)

AKROMID® B28 GM 15/15 1 FR natural (8861) is an UL listed flame retardant PA6, reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS and melamine. Due to its good flowability, it is

Modulus

8.400MPa

Strength

105MPa

Impact

50kJ/m²

AKROMID®

UL
Preliminary

B25 GF 30 1 FR natural (8954)

PA6 GF30 FR(44)

AKROMID® B25 GF 30 1 FR natural (8954) is an UL-listed, flame-retardant, heat-stabilised and 30% glass fibre-reinforced PA6. The material is based on a flame-retardant system that is free of red phosphorus, halogens, melamine, zink borate and PFAS. I

Modulus

11.000MPa

Strength

145MPa

Impact

65kJ/m²

AKROMID®

Preliminary

B3 GF 40 7 natural (8956)

PA6 GF40

AKROMID® B3 GF 40 7 natural (8956) is a 40% glass fiber reinforced Polyamide 6 compound. It is characterized by high stiffness and strength, making it well suited for applications in industrial engineering and automotive components. For adhesive coat

Modulus

13.000MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID®

B3 GF 30 S1 natural (1383)

PA6-I GF30

AKROMID® B3 GF 30 S1 natural (1383) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perf

Modulus

8.000MPa

Strength

125MPa

Impact

110kJ/m²

AKROMID®

B3 GFM 10/20 1 black (2017)

PA6 (GF10+MD20)

AKROMID® B3 GFM 10/20 1 black 950089 (2017) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability

Modulus

6.200MPa

Strength

110MPa

Impact

40kJ/m²

AKROMID®

B3 GM 10/20 1 black (1829)

PA6 (GF10+GB20)

AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage

Modulus

6.200MPa

Strength

115MPa

Impact

45kJ/m²

AKROMID®

B3 GM 15/15 black (1830)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID®

B3 GF 25 1 natural (2463)

PA6 GF25

AKROMID® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²

AKROMID®

B3 GF 25 natural (2471)

PA6 GF25

AKROMID® B3 GF 25 natural (2471) is a 25% glass fibre reinforced polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²