AKROMID®

UL
Preliminary

B28 GM 15/15 1 FR natural (8861) PA6 (GF15+GB15) FR(44)

AKROMID® B28 GM 15/15 1 FR natural (8861) is an UL listed flame retardant PA6, reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS and melamine. Due to its good flowability, it is characterised by easy processability as well as good surface properties. The product is suitable for enclosure applications in the E&E industry due to its low warpage, high stiffness and strength.

Features

flame retardant
surface modified
recycled content
low warpage
easy flow
E&E
sustainable

Regulatory

ul

Properties

Modulus

8.400MPa

Strength

105MPa

Impact

50kJ/m²

Sustainability

Recycled content

ISO 14021

Pre-consumer (PIR)
15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
105 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
50 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
217 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
102 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
775 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,44 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,65 - 0,85 %
0,75 - 0,95 %

Electrical Properties

Dielectric strength

IEC 60243

1 mm | d.a.m.
50 kV/mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

UL

B28 GM 15/15 1 FR black (8750)

PA6 (GF15+GB15) FR(44)

AKROMID® B28 GM 15/15 1 FR black (8750) is an UL listed flame retardant PA6, reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS zinc borate and melamine. Due to its good flowabil

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

AKROMID®

UL

NEXT B28 GM 15/15 1 FR black (8750BMBCI)

PA6 (GF15+GB15) FR(44)

AKROMID® NEXT B28 GM 15/15 1 FR black (8750BMBCI) is a flame retardant PA6, reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS and melamine. Due to its good flowability, it is ch

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

AKROMID®

UL
Preliminary

B28 GM 15/15 1 FR grey (8994)

PA6 (GF15+GB15) FR(44)

AKROMID® B28 GM 15/15 1 FR grey (8894) is an UL listed flame retardant PA6, reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS, zinc borate and melamine. Due to its good flowabil

Modulus

8.200MPa

Strength

85MPa

Impact

30kJ/m²

AKROMID®

B28 GM 5/25 FR black (7492)

PA6 (GF5+GB25) FR(44)

AKROMID® B28 GM 5/25 FR black (7492) is a flame retardant PA6, reinforced with 5% glass fibres and 25% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS and melamine. Due to its good flowability, it is characterised by

Modulus

5.000MPa

Strength

55MPa

Impact

30kJ/m²

AKROMID®

UL
Preliminary

B28 GM 15/15 1 FR orange (8863)

PA6 (GF15+GB15) FR(44)

AKROMID® B28 GM 15/15 1 FR orange (8863) is an UL listed flame retardant PA6, reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS and melamine. Due to its good flowability, it is

Modulus

8.000MPa

Strength

105MPa

Impact

45kJ/m²

AKROMID®

B28 GM 10/20 1 LA black (4790)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LA black (4790) is a 10% glass fiber and 20% glass beads reinforced easy flowing PA 6. It is characterised by a medium stiffness and strength. The material impresses with its laser markability along with very good surface pr

Modulus

5.700MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID®

C28 GF 25 FRT natural (7332)

PA-Blend GF25 FR(44)

C28 GF 25 FRT natural (7332) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/m²

AKROMID®

B3 GM 15/15 natural (3079)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID®

UL
Preliminary

B28 GF 25 9 FR natural (8066)

PA6 GF25 FR(44)

AKROMID® B28 GF 25 9 FR natural (8066) is a flame retardant PA6 with 25% glass fibres. The flame retardant system is free of red phosphorus and halogens, leading to optimised electrical properties for e-mobility applications. This grade is UL listed

Modulus

8.900MPa

Strength

138MPa

Impact

83kJ/m²

AKROMID®

Preliminary

B3 GM 10/20 1 black (8748)

PA6 (GF10+GB20)

AKROMID® B3 GM 10/20 1 black (8748) is a 10% glass fiber and 20% glass beads reinforced easy flowing PA 6. It is characterised by a medium stiffness and strength. The material impresses with very good surface properties and is therefore perfectly s

Modulus

6.300MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID®

UL
Preliminary

B28 GF 30 9 FR natural (8069)

PA6 GF 30 FR(44)

AKROMID® B28 GF 30 9 FR natural (8069) is a flame retardant PA6 with 30% glass fibres. The flame retardant system is free of red phosphorus and halogens, leading to optimised electrical properties for e-mobility applications. This grade is UL listed

Modulus

10.200MPa

Strength

144MPa

Impact

80kJ/m²

AKROMID®

UL

NEXT C3 GF 25 1 FR black (7246BMBCI)

PA66+PA6 GF25 FR(44)

AKROMID® NEXT C3 GF 25 1 FR black (7246BMBCI) is a 25 % glass fiber reinforced, flame retardant and heat stabilised PA6/6.6 blend, colored in black. It is based on a halogen- and antimony trioxide-free flame retardant system that is also free of red

Modulus

9.100MPa

Strength

137MPa

Impact

66kJ/m²