AKROMID®

B3 GK 30 natural (2719)PA6 GB30

AKROMID® B3 GK 30 natural (2719) is a PA 6 filled with 30% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.

Features

surface modified
low warpage

Properties

Modulus

4.400MPa

Strength

70MPa

Impact

30kJ/m²

Sustainability

Recycled content

ISO 14021

Pre-consumer (PIR)
30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
4400 MPa
1820 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
70 MPa
38 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5 %
35 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3140 MPa
1570 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
95 MPa
55 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
3 kJ/m²
5 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | conditioned
961N/30s | d.a.m.
90 MPa
180 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
70 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
185 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Vicat softening temperature B50

ISO 306

50°C/50N
205 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,34 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 %

Water absorption

ISO 62

23°C, saturated
6,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,8 - 1,0 %
0,9 - 1,1 %

Electrical Properties

Volume resistivity

IEC 62631-3-1

d.a.m.
1015 Ω x cm

Surface resistivity

IEC 62631-3-2

d.a.m.
1013 Ω

Rheological Properties

MVR

ISO 1133

275°C/5kg
100 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B3 GM 15/15 natural (3079)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID®

B3 GK 50 natural (3690)

PA6 GB50

AKROMID® B3 GK 50 natural (3690) is a PA 6 filled with 50% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the a

Modulus

5.700MPa

Strength

75MPa

Impact

42kJ/m²

AKROMID®

UL
Preliminary

B28 GM 15/15 1 FR natural (8861)

PA6 (GF15+GB15) FR(44)

AKROMID® B28 GM 15/15 1 FR natural (8861) is an UL listed flame retardant PA6, reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS and melamine. Due to its good flowability, it is

Modulus

8.400MPa

Strength

105MPa

Impact

50kJ/m²

AKROMID®

B3 GF 30 AM natural (8962)

PA6 GF30

AKROMID® B3 GF 30 AM natural (8962) is a 30% glass fiber reinforced polyamide 6 with high stiffness and good sliding properties as well as optimized viscosity. It is suitable for pellet-based large format additive manufacturing processes (LFAM, FGF)

Modulus

8.500MPa

Strength

145MPa

Impact

80kJ/m²

AKROMID®

C28 GF 25 FRT natural (7332)

PA-Blend GF25 FR(44)

C28 GF 25 FRT natural (7332) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/m²

AKROMID®

B3 GK 15 natural (1824)

PA6 GB15

AKROMID® B3 GK 15 natural (1824) is a PA 6 filled with 15% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the a

Modulus

4.000MPa

Strength

85MPa

Impact

30kJ/m²

AKROMID®

B3 GK 30 black (1827)

PA6 GB30

AKROMID® B3 GK 30 black (1827) is a PA 6 filled with 30% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the aut

Modulus

4.500MPa

Strength

75MPa

Impact

38kJ/m²

AKROMID®

B3 GFM 10/20 1 black (2017)

PA6 (GF10+MD20)

AKROMID® B3 GFM 10/20 1 black 950089 (2017) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability

Modulus

6.200MPa

Strength

110MPa

Impact

40kJ/m²

AKROMID®

B3 GM 10/20 1 black (1829)

PA6 (GF10+GB20)

AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage

Modulus

6.200MPa

Strength

115MPa

Impact

45kJ/m²

AKROMID®

B3 GM 15/15 black (1830)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID®

A3 GK 30 natural (3689)

PA66 GB30

AKROMID® A3 GK 30 natural (3689) is a PA 6.6 filled with 30% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the

Modulus

5.000MPa

Strength

90MPa

Impact

28kJ/m²

AKROMID®

A3 GK 30 LA black (4624)

PA66 GB30

AKROMID® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.

Modulus

5.000MPa

Strength

90MPa

Impact

25kJ/m²