AKROLEN®

Preliminary

NEXT PP LGF 40 2 black (8488BMBCI)PP LGF40

AKROLEN® NEXT PP LGF 40 2 black (8488BMBCI) is based on biomass-balanced polypropylene copolymer. With 40% long glass fiber reinforcement, very high stiffness and strength can be achieved. The materials very good surface quality as well as the outstanding UV-stability make it the product of your choice for technical parts which are exposed to UV radiation. The material is certified according to ISCC PLUS. 80% of the fossil raw materials required for manufacturing this product were replaced by sustainable biomass-balanced PP (≙ allocation factor).

Features

biomass balanced
UV-stabilised
Sports & leisure

Regulatory

iscc-plus

Properties

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/m²

Sustainability


Allocation factor

only valid for ISCC PLUS/REDcert² certified products

80 %

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10100 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
81 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
32 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
160 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
165 °C

General properties


Density

ISO 1183

23°C
1,23 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,4 - 0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.