T9 GF 35 1 LT natural (8971)PPA GF 30

AKROMID® T9 GF 35 1 LT natural (8971) is a 35% glass fiber reinforced, laser transparent polyphthalamide with high stiffness and strength, as well as high chemical and temperature resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures, especially in conditioned state.

Features

heat stabilised 130
hydrolysis / chemically stabilised
electrically neutral
laser transparent
reduced moisture
easy flow
E&E
household appliances
Sports & leisure
E-Mobility

Properties

Modulus

12.000MPa

Strength

210MPa

Impact

80kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
12000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
210 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,7 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
80 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
12 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
300 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

General Properties

Density

ISO 1183

23°C
1,41 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,1 - 0,3 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.