AKROMID®

UL
Preliminary

T9 GF 50 8 HU grey (8559)PPA GF50

AKROMID® T9 GF 50 8 HU grey (8559) is a 50% glass fibre reinforced polyphthalamide, colored in grey, similar to RAL 7035. It is characterised by its very high stiffness and strength, even at elevated temperatures up to 120°C. Due to its low moisture absorption, the mechanical properties remain nearly unchanged even in conditioned state. Not only the good creep resistance, but also the hydrolysis and chemical resistance complement the property profile. This UL94 HB all colors listed grade corresponds to the American FDA 21 CFR and is suitable for parts of kitchen and household appliances.

Features

heat stabilised 130
reduced moisture
E&E
household appliances

Regulatory

fdaul

Properties

Modulus

17.200MPa

Strength

245MPa

Impact

90kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17200 MPa
17200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
245 MPa
220 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,2 %
2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
90 kJ/m²
80 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
13 kJ/m²
13 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
270 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
238 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
305 °C

Flammability

Flammability

UL 94

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
HB Class
HB Class

HWI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
PLC 4 PLC
PLC 4 PLC
PLC 4 PLC
PLC 3 PLC

HAI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
PLC 0 PLC
PLC 0 PLC
PLC 0 PLC
PLC 0 PLC

General Properties

Density

ISO 1183

23°C
1,57 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,1 - 0,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,7 - 0,9 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.