AKROLOY®

Preliminary

PARA GF 35 FR orange (8039)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

AKROLOY®

Preliminary

PARA GF 35 FR grey (8200)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

PRECITE®

P3 GF 30 natural (6850)

PBT GF30

PRECITE® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

10.000MPa

Strength

145MPa

Impact

65kJ/m²

PRECITE® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

AKROMID®

Preliminary

NEXT 5.6 3 GF 30 FR black (8465)

PA56 GF30 FR(40)

AKROMID® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.

Modulus

11.000MPa

Strength

137MPa

Impact

64kJ/m²

AKROMID® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.

PRECITE®

Preliminary

E GF 30 4 black (8622)

PET-I GF30

PRECITE®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.400MPa

Strength

135MPa

Impact

70kJ/m²

PRECITE®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

AKROLOY®

Preliminary

PARA GF 35 FR natural (8038)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

AKROMID®

UL
Preliminary

A3 GF 30 8 HU black (8112)

PA66 GF30

AKROMID® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

Modulus

10.500MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

110111280

AKROMID®

A3 GK 30 6 black (6670)PA66 GK30

AKROMID® A3 GK 30 6 black (6670) is a 30% glass beads filled and inorganic high temperature stabilised PA6.6. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.

Features

surface modified
recycled content
low warpage

Properties

Modulus

4.600MPa

Strength

86MPa

Impact

20kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
4600 MPa
1700 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
86 MPa
52 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,2 %
40 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
20 kJ/m²
177 kJ/m²
21 kJ/m²
23 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
2 kJ/m²
4 kJ/m²
2 kJ/m²
2 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
100 °C

Glass transition temperature

ISO 11357-2

DSC, 2nd heating
57 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
800 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
700 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2 %

Molding shrinkage

ISO 294-4

flow
transverse
1,1 %
1,3 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.