AKROLOY®

PARA GF 35 FR black (7496)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

Modulus

14.500MPa

Strength

190MPa

Impact

55kJ/m²

AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

AKROLOY®

Preliminary

PARA GF 35 FR grey (8200)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

AKROMID®

B28 GF 60 1 natural (4775)

PA6 GF60

AKROMID® B28 GF 60 1 natural (4775) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

Modulus

22.000MPa

Strength

260MPa

Impact

100kJ/m²

AKROMID® B28 GF 60 1 natural (4775) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

AKROMID®

UL
Preliminary

A3 GF 30 8 HU black (8112)

PA66 GF30

AKROMID® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

Modulus

10.500MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

AKROMID®

B3 GF 30 RM-M black (3016)

PA6+X GF30

AKROMID® B3 GF 30 RM-M black (3016) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

AKROMID® B3 GF 30 RM-M black (3016) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

AKROMID®

C3 GF 35 1 black (4668)

PA66+PA6 GF35

AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

C3 GF 30 5 XTC black (4686)

PA66+PA6 GF30

AKROMID® C3 GF 30 5 XTC black (4686) - PA6.6/6 blend, 30% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® C3 GF 30 5 XTC black (4686) - PA6.6/6 blend, 30% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry

110111280

AKROTEK®

PK-HM 8 natural (6145)PK

AKROTEK® PK-HM 8 natural (6145) is an unreinforced Polyketone with average flowability. The outstanding friction and wear properties enable the use for demanding components exposed to tribological stress. PK is characterized by its outstanding media resistance, which qualifies it to be used for components that are in contact with chemicals. Moreover the material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR.

Features

hydrolysis / chemically stabilised

Regulatory

eu102011fda

Properties

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
1400 MPa
1400 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
60 MPa
60 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
21 %
21 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 300 %
> 300 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
1500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
60 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
13 kJ/m²
13 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
100 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,24 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,8 - 0,9 %

Water absorption

ISO 62

23°C, saturated
2,0 - 2,4 %

Molding shrinkage

ISO 294-4

flow
transverse
1,4 - 1,6 %
1,5 - 1,7 %

Rheological Properties

MVR

ISO 1133

240°C/2,16kg
6 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.