Select your fitting and find the right compound for your intend
AKROMID®
C3 GF 35 1 black (4668)
PA66+PA6 GF35
AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
11.500MPa
200MPa
95kJ/m²
AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
A3 GM 20/10 4 WIT black (4529)
PA66 (GF20+GB10)
AKROMID® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage
8.200MPa
175MPa
65kJ/m²
AKROMID® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage
AKROLOY®
PA GF 50 natural (6414)
PA66+PA6I/6T GF50
AKROLOY® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
17.000MPa
275MPa
110kJ/m²
AKROLOY® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
AKROMID®
T9 GF 50 black (7601)
PPA GF50
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
17.000MPa
250MPa
95kJ/m²
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
D3 GF 30 1 black (5392)
PA612 GF30
AKROMID® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector
9.500MPa
180MPa
95kJ/m²
AKROMID® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector
AKROLOY®
PA GF 60 black (6418)
PA66+PA6I/6T GF60
AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
21.000MPa
275MPa
100kJ/m²
AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
AKROLOY®
PA CF 40 1 black (8504)
PA66+PA6I/6T CF40
AKROLOY® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications
33.000MPa
310MPa
80kJ/m²
AKROLOY® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications
AKROLOY®
AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.
Properties
17.200MPa
250MPa
105kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 178
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 75
ISO 11357-3
UL 94
FMVSS 302
ISO 1183
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.