Find the right compound
Select your fitting and find the right compound for your intend
AKROMIDĀ®
B3 GF 30 6 black (20009)
PA6 GF30
AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
10.000MPa
180MPa
80kJ/mĀ²
AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
AKROMIDĀ®
D3 GF 30 1 black (5392)
PA612 GF30
AKROMIDĀ® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector
9.500MPa
180MPa
95kJ/mĀ²
AKROMIDĀ® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector
PRECITEĀ®
P3 GFM 20/10 natural (7627)
PBT (GF20+MD10)
PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.
9.300MPa
115MPa
50kJ/mĀ²
PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.
AKROLOYĀ®
PARA GF 35 FR orange (8039)
PARA GF35 FR(40)
AKROLOYĀ® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.
14.500MPa
190MPa
50kJ/mĀ²
AKROLOYĀ® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.
AKROLOYĀ®
PARA GF 35 FR grey (8200)
PARA GF35 FR(40)
AKROLOYĀ® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.
14.500MPa
190MPa
50kJ/mĀ²
AKROLOYĀ® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.
AKROLOYĀ®
PARA GF 35 FR black (7496)
PARA GF35 FR(40)
AKROLOYĀ® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
14.500MPa
190MPa
55kJ/mĀ²
AKROLOYĀ® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
AKROLOYĀ®
PARA GF 35 FR natural (8038)
PARA GF35 FR(40)
AKROLOYĀ® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
14.500MPa
190MPa
50kJ/mĀ²
AKROLOYĀ® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
AKROMIDĀ®
A3 GF 25 3 black (3094)PA66 GF25
AKROMIDĀ® A3 GF 25 3 black (3094) is a 25% glass fibre reinforced, nucleated polyamide 6.6 with high stiffness and strength
Features
Properties
8.500MPa
160MPa
50kJ/mĀ²
Sustainability
Recycled content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Izod notched impact strength
ISO 180/1A
Thermal Properties
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.