AKROMIDĀ®

B3 GF 30 6 black (20009)

PA6 GF30

AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

180MPa

Impact

80kJ/mĀ²

AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

D3 GF 30 1 black (5392)

PA612 GF30

AKROMIDĀ® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector

Modulus

9.500MPa

Strength

180MPa

Impact

95kJ/mĀ²

AKROMIDĀ® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector

PRECITEĀ®

P3 GFM 20/10 natural (7627)

PBT (GF20+MD10)

PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

Modulus

9.300MPa

Strength

115MPa

Impact

50kJ/mĀ²

PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

AKROLOYĀ®

Preliminary

PARA GF 35 FR orange (8039)

PARA GF35 FR(40)

AKROLOYĀ® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/mĀ²

AKROLOYĀ® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

AKROLOYĀ®

Preliminary

PARA GF 35 FR grey (8200)

PARA GF35 FR(40)

AKROLOYĀ® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/mĀ²

AKROLOYĀ® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

AKROLOYĀ®

PARA GF 35 FR black (7496)

PARA GF35 FR(40)

AKROLOYĀ® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

Modulus

14.500MPa

Strength

190MPa

Impact

55kJ/mĀ²

AKROLOYĀ® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

AKROLOYĀ®

Preliminary

PARA GF 35 FR natural (8038)

PARA GF35 FR(40)

AKROLOYĀ® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/mĀ²

AKROLOYĀ® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

110111280

AKROMIDĀ®

UL
Preliminary

B3 GF 30 1 HU LA black (2862)PA6 GF30

AKROMIDĀ® B3 GF 30 1 HU LA black (2862) is a 30% glass fibre reinforced, heat ageing resistant polyamide 6 with high rigidity and strength. This UL94 HB listed grade is suitable for technical components in mechanical engineering and the automotive industry. The material is laser markable.

Features

heat stabilised 130
laser markable
E&E
Sports & leisure

Regulatory

ul

Properties

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
185 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
270 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
95 kJ/mĀ²
85 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
13 kJ/mĀ²
12 kJ/mĀ²

UV Exposure and Water Immersion

UL 746C

UL
f2

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
150 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,36 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 ā„¦

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more