B28 GF 30 natural (4826)

PA6 GF30

AKROMIDĀ® B28 GF 30 natural (4826) - 30% glass fiber reinforced PA 6, easy flowing, technical parts in industrial engineering and automotive industry

Modulus

9.500MPa

Strength

180MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B28 GF 30 natural (4826) - 30% glass fiber reinforced PA 6, easy flowing, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

UL

B3 GF 30 FR natural (7458)

PA6 GF30 FR(40)

AKROMIDĀ® B3 GF 30 FR natural (7458) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion.

Modulus

10.800MPa

Strength

135MPa

Impact

65kJ/mĀ²

AKROMIDĀ® B3 GF 30 FR natural (7458) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion.

AKROMIDĀ®

A3 GM 20/10 4 WIT black (4529)

PA66 (GF20+GB10)

AKROMIDĀ® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage

Modulus

8.200MPa

Strength

175MPa

Impact

65kJ/mĀ²

AKROMIDĀ® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage

PRECITEĀ®

P3 GF 30 natural (6850)

PBT GF30

PRECITEĀ® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

10.000MPa

Strength

145MPa

Impact

65kJ/mĀ²

PRECITEĀ® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

AKROMIDĀ®

T5 GF 35 4 black (7692)

PPA GF35

AKROMIDĀ® T5 GF 35 4 black (7692) is a 35% glass fibre reinforced polyphthalamide with inorganic heat stabilization, very high rigidity and strength, designed for hydrolysis resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up

Modulus

13.500MPa

Strength

220MPa

Impact

70kJ/mĀ²

AKROMIDĀ® T5 GF 35 4 black (7692) is a 35% glass fibre reinforced polyphthalamide with inorganic heat stabilization, very high rigidity and strength, designed for hydrolysis resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up

AKROMIDĀ®

A3 1 S3 black (2768)

PA66+PA6-I

AKROMIDĀ® A3 1 S3 black (2768) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.600MPa

Strength

68MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 1 S3 black (2768) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROTEKĀ®

PK-VM natural (4774)

PK

AKROTEKĀ® PK-VM natural (4774) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.500MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROTEKĀ® PK-VM natural (4774) - Polyketon, Tribology, friction and wear, chemical resistance

110111280

AKROMIDĀ®

A3 GF 60 1 natural (2396)PA66 GF60

AKROMIDĀ® A3 GF 60 1 natural (2396) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color.

Features

heat stabilised 130

Properties

Modulus

20.500MPa

Strength

260MPa

Impact

102kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
20500 MPa
15800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
260 MPa
190 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2 %
2,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
19800 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
400 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
102 kJ/mĀ²
105 kJ/mĀ²
97 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
19 kJ/mĀ²
22 kJ/mĀ²
19 kJ/mĀ²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
330 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
260 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
235 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,71 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,0 - 1,2 %

Water absorption

ISO 62

23Ā°C, saturated
3,2 - 3,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 ā„¦ x cm
1010 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 ā„¦
1010 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.