AKROMID®
T9 GF 50 black (7601)
PPA GF50
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
17.000MPa
250MPa
95kJ/m²
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
A3 GF 30 8 HU natural (8102)
PA66 GF30
AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
10.500MPa
200MPa
75kJ/m²
AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
AKROLOY®
PARA GF 35 FR grey (8200)
PARA GF35 FR(40)
AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.
14.500MPa
190MPa
50kJ/m²
AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.
AKROMID®
C3 GF 35 1 black (4668)
PA66+PA6 GF35
AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
11.500MPa
200MPa
95kJ/m²
AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GF 30 6 black (20009)
PA6 GF30
AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
10.000MPa
180MPa
80kJ/m²
AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
AKROLOY®
PARA GF 35 FR natural (8038)
PARA GF35 FR(40)
AKROLOY® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
14.500MPa
190MPa
50kJ/m²
AKROLOY® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
AKROMID®
T5 GF 35 4 black (7692)
PPA GF35
AKROMID® T5 GF 35 4 black (7692) is a 35% glass fibre reinforced polyphthalamide with inorganic heat stabilization, very high rigidity and strength, designed for hydrolysis resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up
13.500MPa
220MPa
70kJ/m²
AKROMID® T5 GF 35 4 black (7692) is a 35% glass fibre reinforced polyphthalamide with inorganic heat stabilization, very high rigidity and strength, designed for hydrolysis resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up
AKROMID®
B3 GF 15 S3 black (2345)PA6-I GF15
AKROMID® B3 GF 15 S3 black (2345) is a 15% glass fiber reinforced, impact modified Polyamide 6. It is characterised by medium stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 15. It also has good surface properties. The material is therefore perfectly suitable for toughness demanding but high integrated parts with a good surface appearance in the automotive, electro, and furniture industry.
Features
Properties
5.500MPa
110MPa
75kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.