AKROMID®

Preliminary

B+ GF 30 6 LT black (7665)PA6 GF30

AKROMID® B+ GF 30 6 LT black (7665) is a 30% glass fibre reinforced, high-heat stabilised, laser transparent polyamide 6 compound with enhanced mechanical properties, high stiffness and strength in conditioned state to substitute PA66 compounds. For electrical insulation components, AKROMID® materials containing electrically neutral Type 1 stabilizers are recommended.

Features

heat stabilised 160

Properties

Modulus

9.300MPa

Strength

175MPa

Impact

86kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9300 MPa
6000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
175 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
6,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
86 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
19 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,36 g/cm³

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B+ GF 30 6 black (7387)

PA6 GF30

Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds. For electrical insulation components, AKROMID® materials containing electrically neutral Type 1 stabilizers are recom

Modulus

9.500MPa

Strength

180MPa

Impact

86kJ/m²

AKROMID®

Preliminary

B3 GF 40 6 ECO black (8167)

PA6 GF40

AKROMID® B3 GF 40 6 ECO black (8167) is a 40% glass fibre reinforced polyamide 6 with high rigidity and strength. The material is lasermarkable. The formulations of the sustainable ECO products are partly based on regenerated postindustrial feedstoc

Modulus

11.900MPa

Strength

155MPa

Impact

70kJ/m²

AKROMID®

B28 GF 30 6 LT black (8500)

PA6 GF30

AKROMID® B28 GF 30 6 LT black (8500) is a 30% glass fibre reinforced, easy flowing Polyamide 6. The material is characterised by high stiffness and strength. Furthermore, it is UV- and high heat stabilised and therefore perfectly suitable for automot

Modulus

9.800MPa

Strength

185MPa

Impact

90kJ/m²

AKROMID®

Preliminary

B25 GF 30 6 LA black (8953)

PA6 GF30

AKROMID® B25 GF 30 6 LA black (8953) is a 30% glass fiber reinforced easy flowing polyamide 6. It is characterised by a high stiffness and strength even at higher temperature. Furthermore, the material is inorganically high heat stabilised and theref

Modulus

10.000MPa

Strength

175MPa

Impact

100kJ/m²

AKROMID®

B3 GF 30 S1 black (2091)

PA6-I GF30

AKROMID® B3 GF 30 S1 black (2091) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perfec

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/m²

AKROMID®

B3 GF 25 1 black (2484)

PA6 GF25

PLACEHOLDER

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²

AKROMID®

B3 GF 30 black (2493)

PA6 GF30

PLACEHOLDER

Modulus

10.300MPa

Strength

185MPa

Impact

85kJ/m²

AKROMID®

B3 GF 30 1 black (2485)

PA6 GF30

AKROMID® B3 GF 30 1 black (2485) is a 30% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engine

Modulus

10.300MPa

Strength

175MPa

Impact

80kJ/m²

AKROMID®

B3 GF 30 RM-M black (3016)

PA6+X GF30

AKROMID® B3 GF 30 RM-M black (3016) is a 30% glass fiber reinforced polyamide 6 with high stiffness and strength. The material is characterised by a lower moisture uptake compared to standard PA 6 GF 30 compounds which results in less mechanical chan

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

AKROMID®

B3 GF 30 9 RM-M black (3099)

PA6+X GF30

AKROMID® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption

Modulus

10.500MPa

Strength

170MPa

Impact

70kJ/m²

AKROMID®

B3 GF 30 1 L black (4365)

PA6+PP GF30

AKROMID® B3 GF 30 1 L black (4365) is a PA6/PP-blend with reduced density compared to standard PA6 with 30% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are requir

Modulus

8.800MPa

Strength

140MPa

Impact

60kJ/m²

AKROMID®

B3 GF 30 S1 LA black (4446)

PA6-I GF30

AKROMID® B3 GF 30 S1 LA black (4446) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by a medium impact strength as well as a high stiffness and strength. Furthermore, the material impresses with its laser markabilit

Modulus

8.400MPa

Strength

150MPa

Impact

110kJ/m²