AKROMID®

B3 GF 30 9 RM-M black (3099)PA6+X GF30

AKROMID® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption

Features

reduced moisture
process improved

Properties

Modulus

10.500MPa

Strength

170MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10500 MPa
7500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
170 MPa
115 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,6 %
4,2 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
9600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
70 kJ/m²
70 kJ/m²
65 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
12 kJ/m²
13 kJ/m²
10 kJ/m²
10 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
160 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 °C

Flammability

Flammability

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,41 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,6 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B3 GF 30 RM-M black (3016)

PA6+X GF30

AKROMID® B3 GF 30 RM-M black (3016) is a 30% glass fiber reinforced polyamide 6 with high stiffness and strength. The material is characterised by a lower moisture uptake compared to standard PA 6 GF 30 compounds which results in less mechanical chan

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

AKROMID®

UL
Preliminary

T91 GF 30 FR black (8184)

PPA GF30 FR(44)

AKROMID® T91 GF 30 FR black (8184) is an easy flow, flame retardant and 30% glass fiber reinforced Polyamide 9T with high stiffness and strength. This material is based on the latest flame retardant technology, that is free of red phosphorous, melami

Modulus

11.000MPa

Strength

140MPa

Impact

40kJ/m²

AKROMID®

UL
Preliminary

B25 GF 30 1 FR black (9014)

PA6 GF30 FR(44)

AKROMID® B25 GF 30 1 FR black (9014) is an UL listed, flame-retardant, heat-stabilised and 30% glass fibre-reinforced PA6. The material is based on a flame-retardant system that is free of red phosphorus, halogens, melamine, zinc borate and PFAS. It

Modulus

11.000MPa

Strength

135MPa

Impact

60kJ/m²

AKROMID®

Preliminary

NEXT T91 GF 30 FR black (8184BMBCI)

PPA GF30 FR(44)

AKROMID® NEXT T91 GF 30 FR black (8184BMBCI) is an easy flow, flame retardant and 30% glass fiber reinforced Polyamide 9T with high stiffness and strength. This material is based on the latest flame retardant technology, that is free of red phosphoro

Modulus

11.000MPa

Strength

140MPa

Impact

40kJ/m²

AKROMID®

B3 GF 30 S1 black (2091)

PA6-I GF30

AKROMID® B3 GF 30 S1 black (2091) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perfec

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/m²

AKROMID®

B3 GF 25 1 black (2484)

PA6 GF25

PLACEHOLDER

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²

AKROMID®

B3 GF 30 black (2493)

PA6 GF30

PLACEHOLDER

Modulus

10.300MPa

Strength

185MPa

Impact

85kJ/m²

AKROMID®

B3 GF 30 1 black (2485)

PA6 GF30

AKROMID® B3 GF 30 1 black (2485) is a 30% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engine

Modulus

10.300MPa

Strength

175MPa

Impact

80kJ/m²

AKROMID®

B3 GF 50 RM-M black (3146)

PA6+X GF50

AKROMID® B3 GF 50 RM-M black (3146) is a 50% glass fiber reinforced polyamide 6. The material is characterised by very high stiffness and strength as well as reduced moisture absorption. As a result, there will be less changes of the mechanical prope

Modulus

17.000MPa

Strength

210MPa

Impact

70kJ/m²

AKROMID®

B3 GF 30 RM-M natural (3291)

PA6+X GF30

AKROMID® B3 GF 30 RM-M natural (3291) is a 30% glass fiber reinforced polyamide 6 with high stiffness and strength. The material is characterised by a lower moisture uptake compared to standard PA 6 GF 30 compounds which results in less mechanical ch

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

AKROMID®

B3 GF 30 1 L black (4365)

PA6+PP GF30

AKROMID® B3 GF 30 1 L black (4365) is a PA6/PP-blend with reduced density compared to standard PA6 with 30% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are requir

Modulus

8.800MPa

Strength

140MPa

Impact

60kJ/m²

AKROMID®

B3 GF 30 S1 LA black (4446)

PA6-I GF30

AKROMID® B3 GF 30 S1 LA black (4446) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by a medium impact strength as well as a high stiffness and strength. Furthermore, the material impresses with its laser markabilit

Modulus

8.400MPa

Strength

150MPa

Impact

110kJ/m²