AKROMID®

Preliminary

B3 GF 40 6 ECO black (8167)PA6 GF40

AKROMID® B3 GF 40 6 ECO black (8167) is a 40% glass fibre reinforced polyamide 6 with high rigidity and strength. The material is lasermarkable. The formulations of the sustainable ECO products are partly based on regenerated postindustrial feedstock. The use of by-products further contributes to reducing the CO₂ footprint. For electrical insulation components, AKROMID® materials containing electrically neutral Type 1 stabilizers are recommended.

Features

heat stabilised 160
sustainable

Properties

Modulus

11.900MPa

Strength

155MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
11900 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
155 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,3 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
10 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

General Properties

Density

ISO 1183

23°C
1,46 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,5 - 1,8 %

Water absorption

ISO 62

23°C, saturated
5,2 - 5,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B+ GF 30 6 black (7387)

PA6 GF30

Anorganic, high-heat stabilized PA6 compound with enhanced mechanical properties in conditioned state to substitute PA 66 compounds. For electrical insulation components, AKROMID® materials containing electrically neutral Type 1 stabilizers are recom

Modulus

9.500MPa

Strength

180MPa

Impact

86kJ/m²

AKROMID®

Preliminary

B+ GF 30 6 LT black (7665)

PA6 GF30

AKROMID® B+ GF 30 6 LT black (7665) is a 30% glass fibre reinforced, high-heat stabilised, laser transparent polyamide 6 compound with enhanced mechanical properties, high stiffness and strength in conditioned state to substitute PA66 compounds. For

Modulus

9.300MPa

Strength

175MPa

Impact

86kJ/m²

AKROMID®

Preliminary

B3 GF 30 ECO black (7923)

PA6 GF30

AKROMID® B3 GF 30 ECO black (7923) is a 30% glass fibre-reinforced, heat-stabilised polyamide 6. This compound is suitable for technical components in mechanical engineering and automotive industry with demands for high stiffness and strength. The fo

Modulus

9.500MPa

Strength

155MPa

Impact

75kJ/m²

AKROMID®

Preliminary

A3 GF 30 6 ECO black (8160)

PA66 GF30

AKROMID® A3 GF 30 6 ECO black (8160) is a 30% glass fibre-reinforced, inorganically heat-stabilised polyamide 6.6. The compound is suitable for technical components in mechanical engineering and the automotive industry with demands for high stiffness

Modulus

9.000MPa

Strength

150MPa

Impact

50kJ/m²

AKROMID®

B28 GF 30 6 LT black (8500)

PA6 GF30

AKROMID® B28 GF 30 6 LT black (8500) is a 30% glass fibre reinforced, easy flowing Polyamide 6. The material is characterised by high stiffness and strength. Furthermore, it is UV- and high heat stabilised and therefore perfectly suitable for automot

Modulus

9.800MPa

Strength

185MPa

Impact

90kJ/m²

AKROMID®

Preliminary

NEXT B28 GF 30 9 FR black (8342BMBCI)

PA6 GF30 FR(44)

AKROMID® NEXT B28 GF 30 9 FR black (8342BMBCI) is a flame retardant PA6 with 30% glass fibres. The flame retardant system is free of red phosphorus and halogens, leading to optimised electrical properties for e-mobility applications. This grade meet

Modulus

10.200MPa

Strength

148MPa

Impact

75kJ/m²

AKROMID®

NEXT B3 GF 30 1 black (2485BMBCI)

PA6 GF30

AKROMID® NEXT B3 GF 30 1 black (2485BMBCI) is a 30 % glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in indust

Modulus

10.300MPa

Strength

185MPa

Impact

75kJ/m²

AKROMID®

NEXT B28 GF 30 2 black (7059BMBCI)

PA6 GF30

AKROMID®NEXT B28 GF 30 2 black (7059BMBCI) is a 30% glass fiber reinforced, easy flowing polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is UV and heat stabilised and therefore perfectly suitable for techn

Modulus

10.000MPa

Strength

180MPa

Impact

70kJ/m²

AKROMID®

Preliminary

B3 GF 30 1 L ECO black (8967)

PA6+PP GF30

AKROMID® B3 GF 30 1 L ECO black (8967) is a PA6+PP blend with post consumer recycled content and reduced density. With 30% glass fiber reinforcement this material is suitable for components with high strength and stiffness where weight reduction is r

Modulus

9.000MPa

Strength

140MPa

Impact

57kJ/m²

AKROMID®

Preliminary

B25 GF 30 6 LA black (8953)

PA6 GF30

AKROMID® B25 GF 30 6 LA black (8953) is a 30% glass fiber reinforced easy flowing polyamide 6. It is characterised by a high stiffness and strength even at higher temperature. Furthermore, the material is inorganically high heat stabilised and theref

Modulus

10.000MPa

Strength

175MPa

Impact

100kJ/m²

AKROMID®

Preliminary

B3 GF 30 ECO black (9172)

PA6 GF30

AKROMID® B3 GF 30 ECO black (9172) is a 30% glass fibre-reinforced, heat-stabilised polyamide 6 with a basic laser markability. The formulation of this sustainable ECO product is partly based on post-consumer recycled feedstock and thus contribute to

Modulus

10.000MPa

Strength

160MPa

Impact

60kJ/m²

AKROMID®

B3 GF 30 S1 black (2091)

PA6-I GF30

AKROMID® B3 GF 30 S1 black (2091) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perfec

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/m²