B28 GF 30 9 FR natural (8069)

PA6 GF 30 FR(40)

AKROMID® B28 GF 30 9 FR natural (8069) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

Modulus

10.200MPa

Strength

144MPa

Impact

80kJ/m²

AKROMID® B28 GF 30 9 FR natural (8069) - PA6, 30% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, e-mobility.

PRECITE®

Preliminary

E GF 45 ECO black (8284)

PET GF45

PRECITE® E GF 45 ECO black (8284) - PET, 45% glass fiber, very high stiffness, high toughness, good dimensional stability, good chemical resistance, automotive, E&E, industrial, household, sport & leisure.

Modulus

16.100MPa

Strength

200MPa

Impact

65kJ/m²

PRECITE® E GF 45 ECO black (8284) - PET, 45% glass fiber, very high stiffness, high toughness, good dimensional stability, good chemical resistance, automotive, E&E, industrial, household, sport & leisure.

AKROMID®

B3 GF 30 S1 LA black (4446)

PA6-I GF30

AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

Modulus

8.400MPa

Strength

150MPa

Impact

110kJ/m²

AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

AKROLOY®

PA GF 40 black (6416)

PA66+PA6I/6T GF40

AKROLOY® PA GF 40 black (6416) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

13.000MPa

Strength

235MPa

Impact

95kJ/m²

AKROLOY® PA GF 40 black (6416) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROLOY®

PA FGF 50 black (6546)

PA66+PA6I/6T FGF50

AKROLOY® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90° to the flow direction

Modulus

17.000MPa

Strength

265MPa

Impact

100kJ/m²

AKROLOY® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90° to the flow direction

PRECITE®

Preliminary

P3 ICF 30 black (6948)

PBT CF 30

PRECITE® P3 ICF 30 black (6948) - PBT, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

23.500MPa

Strength

175MPa

Impact

50kJ/m²

PRECITE® P3 ICF 30 black (6948) - PBT, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

PRECITE®

Preliminary

E GF 40 natural (7304)

PET GF 40

PRECITE® E GF 40 natural (7304) - PET, 40 % glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

15.000MPa

Strength

195MPa

Impact

64kJ/m²

PRECITE® E GF 40 natural (7304) - PET, 40 % glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

119202180

AKROLOY®

PA ICF 30 black (5269)PA66+PA6I/6T CF30

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Features

low warpage
reduced moisture

Properties

Modulus

25.000MPa

Strength

220MPa

Impact

50kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
25000 MPa
23000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
220 MPa
200 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,5 %
1,6 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
21000 MPa
21000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
320 MPa
300 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2 %
2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
50 kJ/m²
50 kJ/m²
40 kJ/m²
40 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
7 kJ/m²
7 kJ/m²
6 kJ/m²
6 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,29 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,6 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,3 - 0,5 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
104 Ω
104 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more