AKROMID®

Preliminary

B3 GM 20/10 1 WIT black (8139)PA6 (GF20+GB10)

AKROMID® B3 GM 20/10 1 WIT black (8139) is a 20% glass fiber and 10% glass bead reinforced polyamide 6. It is characterized by high rigidity and strength. The material also convinces with a good surface and low tendency to warp and can be processed using a water injection process. In addition, the material is heat stabilized and is therefore ideally suited for technical components in the automotive and engineering industry.

Features

heat stabilised 130
surface modified
low warpage
fluid injection (GIT/WIT/FIT)

Properties

Modulus

7.400MPa

Strength

140MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
7400 MPa
4200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
140 MPa
80 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
10 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
10 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
> 650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,35 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B3 GM 10/20 1 black (1829)

PA6 (GF10+GB20)

AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage

Modulus

6.200MPa

Strength

115MPa

Impact

45kJ/m²

AKROMID®

B28 GM 10/20 1 LT black (7749)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LT black (7749) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, lasertransparent and laser markable polyamide 6 with good surface and low warpage

Modulus

6.300MPa

Strength

110MPa

Impact

40kJ/m²

AKROMID®

B3 GFM 10/20 1 black (2017)

PA6 (GF10+MD20)

AKROMID® B3 GFM 10/20 1 black 950089 (2017) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability

Modulus

6.200MPa

Strength

110MPa

Impact

40kJ/m²

AKROMID®

B3 GM 15/15 black (1830)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID®

A3 GM 20/10 4 WIT black (4529)

PA66 (GF20+GB10)

AKROMID® A3 GM 20/10 4 WIT black (4529) is a 20% glass fiber and 10% glass bead reinforced polyamide 6.6. It is characterized by high rigidity and strength. The material also convinces with a good surface and low tendency to warp and can be processed

Modulus

8.200MPa

Strength

175MPa

Impact

65kJ/m²

AKROMID®

B3 GF 30 1 GIT black (4598)

PA6 GF30

AKROMID® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding.

Modulus

9.500MPa

Strength

175MPa

Impact

NA

AKROMID®

B28 GF 33 1 GIT black (6846)

PA6 GF33

AKROMID® B28 GF 33 1 GIT black (6846) is a 33% glass fiber reinforced, heat-stabilized polyamide 6. It is characterized by high rigidity and strength. The material also impresses with its very good processability using the internal gas pressure proce

Modulus

10.500MPa

Strength

190MPa

Impact

95kJ/m²

AKROMID®

B28 GM 10/20 1 LA black (4790)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LA black (4790) is a 10% glass fiber and 20% glass beads reinforced easy flowing PA 6. It is characterised by a medium stiffness and strength. The material impresses with its laser markability along with very good surface pr

Modulus

5.700MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID®

B3 GF 30 1 GIT LA black (8278)

PA6 GF30

AKROMID® B3 GF 30 1 GIT LA black (8278) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding. The material is lasermarkable.

Modulus

9.300MPa

Strength

175MPa

Impact

NA

AKROMID®

UL

B28 GM 15/15 1 FR black (8750)

PA6 (GF15+GB15) FR(44)

AKROMID® B28 GM 15/15 1 FR black (8750) is an UL listed flame retardant PA6, reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS zinc borate and melamine. Due to its good flowabil

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

AKROMID®

UL

NEXT B28 GM 15/15 1 FR black (8750BMBCI)

PA6 (GF15+GB15) FR(44)

AKROMID® NEXT B28 GM 15/15 1 FR black (8750BMBCI) is a flame retardant PA6, reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS and melamine. Due to its good flowability, it is ch

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

AKROMID®

B3 GM 15/15 natural (3079)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²