AKROMID®

B28 GM 10/20 1 LT black (7749)PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LT black (7749) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, lasertransparent and laser markable polyamide 6 with good surface and low warpage

Features

heat stabilised 130
laser markable
laser transparent
surface modified
low warpage

Properties

Modulus

6.300MPa

Strength

110MPa

Impact

40kJ/m²

Sustainability

Recycled content

ISO 14021

Pre-consumer (PIR)
20 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
6300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
40 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,35 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B3 GM 10/20 1 black (1829)

PA6 (GF10+GB20)

AKROMID® B3 GM 10/20 1 black 950058 (1829) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised polyamide 6 with good surface and low warpage

Modulus

6.200MPa

Strength

115MPa

Impact

45kJ/m²

AKROMID®

B28 GM 10/20 1 LA black (4790)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LA black (4790) is a 10% glass fiber and 20% glass beads reinforced easy flowing PA 6. It is characterised by a medium stiffness and strength. The material impresses with its laser markability along with very good surface pr

Modulus

5.700MPa

Strength

110MPa

Impact

30kJ/m²

AKROMID®

Preliminary

B3 GM 20/10 1 WIT black (8139)

PA6 (GF20+GB10)

AKROMID® B3 GM 20/10 1 WIT black (8139) is a 20% glass fiber and 10% glass bead reinforced polyamide 6. It is characterized by high rigidity and strength. The material also convinces with a good surface and low tendency to warp and can be processed u

Modulus

7.400MPa

Strength

140MPa

Impact

70kJ/m²

AKROMID®

UL

B28 GM 15/15 1 FR black (8750)

PA6 (GF15+GB15) FR(44)

AKROMID® B28 GM 15/15 1 FR black (8750) is an UL listed flame retardant PA6, reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS zinc borate and melamine. Due to its good flowabil

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

AKROMID®

UL

NEXT B28 GM 15/15 1 FR black (8750BMBCI)

PA6 (GF15+GB15) FR(44)

AKROMID® NEXT B28 GM 15/15 1 FR black (8750BMBCI) is a flame retardant PA6, reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS and melamine. Due to its good flowability, it is ch

Modulus

8.400MPa

Strength

105MPa

Impact

45kJ/m²

AKROMID®

B3 GFM 10/20 1 black (2017)

PA6 (GF10+MD20)

AKROMID® B3 GFM 10/20 1 black 950089 (2017) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability

Modulus

6.200MPa

Strength

110MPa

Impact

40kJ/m²

AKROMID®

B3 GM 15/15 black (1830)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID®

B3 GF 30 1 GIT LA black (8278)

PA6 GF30

AKROMID® B3 GF 30 1 GIT LA black (8278) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding. The material is lasermarkable.

Modulus

9.300MPa

Strength

175MPa

Impact

NA

AKROMID®

B3 GF 30 1 S1 LA black (8829)

PA6-I GF30

AKROMID® B3 GF 30 1 S1 LA black (8829) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by a medium impact strength as well as a high stiffness and strength. Furthermore, the material impresses with its laser markabil

Modulus

8.400MPa

Strength

140MPa

Impact

95kJ/m²

AKROMID®

UL
Preliminary

B28 GM 15/15 1 FR grey (8994)

PA6 (GF15+GB15) FR(44)

AKROMID® B28 GM 15/15 1 FR grey (8894) is an UL listed flame retardant PA6, reinforced with 15% glass fibres and 15% glass beads. The flame retardant system is free of halogens, red phosphorus, PFAS, zinc borate and melamine. Due to its good flowabil

Modulus

8.200MPa

Strength

85MPa

Impact

30kJ/m²

AKROMID®

B3 GM 15/15 natural (3079)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID®

A3 GM 20/10 4 WIT black (4529)

PA66 (GF20+GB10)

AKROMID® A3 GM 20/10 4 WIT black (4529) is a 20% glass fiber and 10% glass bead reinforced polyamide 6.6. It is characterized by high rigidity and strength. The material also convinces with a good surface and low tendency to warp and can be processed

Modulus

8.200MPa

Strength

175MPa

Impact

65kJ/m²