AKROMID®

Preliminary

B3 ICF 10 9 black (7220)PA6 CF10

AKROMID® B3 ICF 10 9 black (7220) is a 10% carbon fibre reinforced, heat-stabilised and process-optimised polyamide 6. Thanks to its low density and high mechanical durability, this material is ideal for load-bearing components in the automotive industry, such as lightweight structural parts, as well as for sports and leisure applications, including high-stress sports equipment and technical components.

Features

heat stabilised 130
sustainable

Properties

Modulus

7.600MPa

Strength

120MPa

Impact

35kJ/m²

Sustainability

Recycled content

10 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
7600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,0 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
7000 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
35 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
4 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
190 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,17 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,5 - 0,6 %
0,7 - 0,8 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
210 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B3 ICF 10 1 black (6194)

PA6 CF10

AKROMID® B3 ICF 10 1 black (6194) is a heat stabilised Polyamide 6 with 10% carbon fiber reinforcement, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Thanks

Modulus

8.500MPa

Strength

125MPa

Impact

45kJ/m²

AKROMID®

Preliminary

B3 ICF 10 AM black (8336)

PA6 CF10

AKROMID® B3 ICF 10 AM black (8336) is a Polyamide 6 with 10% carbon fiber reinforcement, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. It is suitable for a

Modulus

8.000MPa

Strength

120MPa

Impact

45kJ/m²

AKROMID®

B3 ICF 20 1 L black (5296)

PA6+PP CF20

AKROMID® B3 ICF 20 1 L black (5296) is a 20% carbon fibre reinforced, heat stabilised polyamide-blend with high flexural strength, good sliding properties and a reduced density compared to standard PA6 ICF 20

Modulus

14.200MPa

Strength

140MPa

Impact

50kJ/m²

AKROMID®

Preliminary

B3 1 L ECO black (8969)

PA6+PP(REC)

AKROMID® B3 1 L ECO black (8969) is a PA6+PP blend with post consumer recycled content and reduced density. This material is suitable for components where weight reduction is required.

Modulus

2.500MPa

Strength

60MPa

Impact

180kJ/m²

AKROMID®

B3 GF 10 1 black (3658)

PA6 GF10

AKROMID® B3 GF 10 1 black (3658) is a 10% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

Modulus

4.800MPa

Strength

105MPa

Impact

47kJ/m²

AKROMID®

B3 ICF 40 black (5020)

PA6 CF40

AKROMID® B3 ICF 40 black (5020) is a high performance Polyamide 6 with 40% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Thanks

Modulus

30.000MPa

Strength

220MPa

Impact

60kJ/m²

AKROMID®

B3 ICF 20 black (5103)

PA6 CF20

AKROMID® B3 ICF 20 black (5103) is a high performance Polyamide 6 with 20% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Thanks

Modulus

13.500MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID®

B3 ICF 30 black (5119)

PA6 CF30

AKROMID® B3 ICF 30 black (5119) is a high performance Polyamide 6 with 30% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Thanks

Modulus

23.000MPa

Strength

200MPa

Impact

55kJ/m²

AKROMID®

B3 ICF 20 LF black (6695)

PA6 CF20

AKROMID® B3 ICF 20 LF black (6695) is a high performance Polyamide 6 with 20% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Due

Modulus

15.000MPa

Strength

175MPa

Impact

50kJ/m²

PRECITE®

Preliminary

P3 ICF 10 black (6946)

PBT CF10

PRECITE® P3 ICF 10 black (6946) is a PBT reinforced with 10% recycled carbon fiber with excellent dimensional stability. Thanks to its low moisture absorption, PRECITE® achieves consistent mechanical and electrical properties, even under changing cl

Modulus

7.500MPa

Strength

100MPa

Impact

30kJ/m²

AKROMID®

B3 ICF 30 AM black (7451)

PA6 CF30

AKROMID® B3 ICF 30 AM black (7451) is a high performance Polyamide 6 with 30% carbon fiber reinforcement and optimized viscosity for 3D printing, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an o

Modulus

20.000MPa

Strength

190MPa

Impact

45kJ/m²

AKROMID®

Preliminary

B3 GF 30 ECO black (7923)

PA6 GF30

AKROMID® B3 GF 30 ECO black (7923) is a 30% glass fibre-reinforced, heat-stabilised polyamide 6. This compound is suitable for technical components in mechanical engineering and automotive industry with demands for high stiffness and strength. The fo

Modulus

9.500MPa

Strength

155MPa

Impact

75kJ/m²