AKROMID^®

B3 ICF 40 black (5020)PA6 CF40

AKROMID® B3 ICF 40 black (5020) is a high performance Polyamide 6 with 40% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Thanks to its low density and high mechanical durability, this material is ideal for load-bearing components in the automotive industry, such as lightweight structural parts, as well as for sports and leisure applications, including high-stress sports equipment and technical components.

Features

recycled content

reduced density

antistatic/conductive

tribological modified

Sports & leisure

lightweight construction

Properties

Modulus

30.000MPa

Strength

220MPa

Impact

60kJ/m²

Sustainability

Recycled content

40 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

30000 MPa

14000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

220 MPa

135 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

1,7 %

3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

25000 MPa

17000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

320 MPa

215 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

1,8 %

2,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

60 kJ/m²

65 kJ/m²

50 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

10 kJ/m²

15 kJ/m²

8 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

210 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

220 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel

23°C to 80°C | transverse

0,17 10⁻⁴/K

0,73 10⁻⁴/K

Thermal conductivity

DIN 52612

0,41 W/mK

Flammability

UL 94

1,6 mm Wall thickness

HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General Properties

Density

ISO 1183

23°C

1,31 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

1,8 - 2,0 %

Molding shrinkage

ISO 294-4

flow

transverse

0,1 - 0,3 %

0,4 - 0,6 %

Electrical Properties

Surface resistivity

IEC 62631-3-2

d.a.m.

conditioned

10³ Ω

Rheological Properties

Flowability

AKRO

2 mm Thickness

300 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.