AKROMID®

UL
Preliminary

A3 S1 black (8983)PA66-I

AKROMID® A3 S1 black (8983) is an UL94 HB listed unreinforced, impact modified Polyamide 6.6. The material is characterised by a very high impact strength even at low temperatures and therefore perfectly suitable for connecting and fixing systems which are used in the automotive and electro industry and that are exposed to high loading speeds.

Regulatory

ul

Properties

Modulus

1.800MPa

Strength

50MPa

Impact

Na

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1800 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
> 50 %

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
90 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Flammability

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,07 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,9 - 2,1 %

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.