AKROMID®

A3 1 S3 black (21002)PA66-I

AKROMID® A3 1 S3 black (21002) is an unreinforced, impact modified Polyamide 66. It is characterised by a medium dry impact strength and good surface quality. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry.

Features

heat stabilised 130
impact modified
surface modified

Properties

Modulus

2.300MPa

Strength

58MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2300 MPa
800 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
58 MPa
38 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
33 %
> 200 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2200 MPa
800 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
85 MPa
35 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
13 kJ/m²
100 kJ/m²
8 kJ/m²
9 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,1 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2 %

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

A3 1 S3 black (1139)

PA66-I

AKROMID® A3 1 S3 black (1139) is an unreinforced, impact modified Polyamide 6.6. It is characterised by a medium dry impact strength whilst maintaining good flowability. Furthermore, the material is heat stabilised and therefore perfectly suitable fo

Modulus

2.700MPa

Strength

63MPa

Impact

180kJ/m²

AKROMID®

A3 1 S3 black (2768)

PA66+PA6-I

AKROMID® A3 1 S3 black (2768) is an unreinforced, impact modified polyamide 6.6/6 blend. It is characterised by a medium dry impact strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing syst

Modulus

2.600MPa

Strength

68MPa

Impact

180kJ/m²

AKROMID®

Preliminary

A3 1 S3 ECO black (8740)

PA66-I

AKROMID® A3 1 S3 ECO black (8740) is an unreinforced, impact modified Polyamide 66 with improved CO₂ reduced-footprint, achieved through the use of chemically recycled polymer. The formulations of the sustainable ECO products are partly based on rege

Modulus

2.300MPa

Strength

60MPa

Impact

180kJ/m²

AKROMID®

UL

A3 S1 black (1071)

PA66-I

AKROMID® A3 S1 black 950089 (1071) is an UL94 HB listed unreinforced, impact modified Polyamide 6.6. The material is characterised by a very high impact strength even at low temperatures and therefore perfectly suitable for connecting and fixing syst

Modulus

2.000MPa

Strength

50MPa

Impact

180kJ/m²

AKROMID®

A3 5 S3 15 black (1434)

PA66-I

AKROMID® A3 5 S3 15 black 950058 (1434) is an unreinforced, impact modified Polyamide 6.6. It is characterised by a medium dry impact strength. Furthermore, the material is high heat stabilised and therefore perfectly suitable for connecting and fixi

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/m²

AKROMID®

A3 1 black (2417)

PA66

AKROMID® A3 1 black (2417) is a heat stabilised, unreinforced polyamide 6.6

Modulus

3.200MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID®

A3 1 S3 natural (2847)

PA66+PA6-I

AKROMID® A3 1 S3 natural (2847) is an unreinforced, impact modified Polyamide 6.6. It is characterised by a medium dry impact strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems wh

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/m²

AKROMID®

A3 1 S3 15 natural (2892)

PA66-I

AKROMID® A3 1 S3 15 natural (2892) is an unreinforced, impact modified Polyamide 6.6. It is characterised by a medium dry impact strength whilst maintaining good flowability. Furthermore, the material is heat stabilised and therefore perfectly suitab

Modulus

2.700MPa

Strength

63MPa

Impact

180kJ/m²

AKROMID®

A3 GF 30 1 S3 black (3502)

PA66-I GF30

AKROMID® A3 GF 30 1 S3 black (3502) is a 30% glass fiber reinforced, impact modified Polyamide 6.6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6.6 GF 30. Furthermore, the material

Modulus

8.000MPa

Strength

170MPa

Impact

100kJ/m²

AKROMID®

A3 1 L black (4652)

PA66+PP

AKROMID® A3 1 L black (4652) is an unreinforced PA6.6/PP-blend with reduced density compared to standard PA6.6. The material can be used where weight and cost reduction is required.

Modulus

2.300MPa

Strength

54MPa

Impact

180kJ/m²

AKROMID®

A3 1 S3 grey (2955)

PA66+PA6-I

AKROMID® A3 1 S3 grey (2955) is an unreinforced, impact modified Polyamide 6.6 in grey color, similar to RAL 7011. It is characterised by a medium dry impact strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for

Modulus

2.500MPa

Strength

68MPa

Impact

180kJ/m²

AKROMID®

C3 5 S3 black (4605)

PA66+PA6

AKROMID® C3 5 S3 black (4605) is an unreinforced, high temperature stabilised, dry impact resistant polyamide 6.6/6-Blend. For electrical insulation components, AKROMID® materials containing electrically neutral Type 1 stabilizers are recommended.

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/m²