Find the right compound
Select your fitting and find the right compound for your intend
AKROLOY®
PA ICF 30 black (5269)
PA66+PA6I/6T CF30
AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
25.000MPa
220MPa
50kJ/m²
AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
AKROMID®
B28 GF 30 9 natural (6614)
PA6 GF30
AKROMID® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry
10.300MPa
185MPa
95kJ/m²
AKROMID® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry
AKROMID®
B28 GF 50 9 natural (6570)
PA6 GF50
AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release
17.000MPa
250MPa
115kJ/m²
AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release
AKROLOY®
PA FGF 50 black (6546)
PA66+PA6I/6T FGF50
AKROLOY® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90° to the flow direction
17.000MPa
265MPa
100kJ/m²
AKROLOY® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90° to the flow direction
AKROMID®
B3 GF 30 1 PST black (6647)
PA6 GF30
AKROMID® B3 GF 30 1 PST schwarz (6647) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and optimized for adhesion to PST (Plasma Seal-Tight®) coatings developed by Plasmatreat®
10.300MPa
185MPa
95kJ/m²
AKROMID® B3 GF 30 1 PST schwarz (6647) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and optimized for adhesion to PST (Plasma Seal-Tight®) coatings developed by Plasmatreat®
PRECITE®
P1 natural (7010)
PBT
PRECITE® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.
2.400MPa
55MPa
180kJ/m²
PRECITE® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.
PRECITE®
P1 GF 30 natural (7062)
PBT GF30
PRECITE® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.
9.800MPa
150MPa
75kJ/m²
PRECITE® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.
AKROMID®
B3 GF 15 1 L natural (4690)PA6+PP GF15
AKROMID® B3 GF 15 1 L natural (4690) is a PA6/PP-blend with reduced density compared to standard PA6 with 15% glass fibre reinforcement. The material is suitable for components with average strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMID® B3 GF 15 1 L natural (4690) is particularly superior to calcium chloride (CaCl₂).
Features
Properties
5.200MPa
110MPa
60kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.