AKROMIDĀ®

B28 GF 50 natural (4842)

PA6 GF50

AKROMIDĀ® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

Modulus

16.500MPa

Strength

250MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

AKROMIDĀ®

B28 GF 30 9 natural (6614)

PA6 GF30

AKROMIDĀ® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry

AKROLOYĀ®

PA FGF 50 black (6546)

PA66+PA6I/6T FGF50

AKROLOYĀ® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90Ā° to the flow direction

Modulus

17.000MPa

Strength

265MPa

Impact

100kJ/mĀ²

AKROLOYĀ® PA FGF 50 black (6546) - semi-aromatic polyamide blend, 50% flat glass fiber reinforced,improved properties 90Ā° to the flow direction

AKROMIDĀ®

UL
Preliminary

A3 GF 50 HU natural (6662)

PA66 GF50

AKROMIDĀ® A3 GF 50 HU natural (6662) is a 50% glass fibre reinforced, heat stabilised polyamide 6.6 with very high rigidity and strength, light inherent color and listet at UL in all colors

Modulus

18.000MPa

Strength

255MPa

Impact

105kJ/mĀ²

AKROMIDĀ® A3 GF 50 HU natural (6662) is a 50% glass fibre reinforced, heat stabilised polyamide 6.6 with very high rigidity and strength, light inherent color and listet at UL in all colors

PRECITEĀ®

Preliminary

E GF 20 black (7360)

PET GF 20

PRECITEĀ® E GF 20 black (7360) - PET, 20 % glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

7.800MPa

Strength

NA

Impact

35kJ/mĀ²

PRECITEĀ® E GF 20 black (7360) - PET, 20 % glass fibre, good stiffness, good toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

PRECITEĀ®

Preliminary

V GF 20 2 black (7738)

PBT-ASA- GF 20

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

6.500MPa

Strength

110MPa

Impact

50kJ/mĀ²

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

PRECITEĀ®

Preliminary

E GF 45 natural (7305)

PET GF 45

PRECITEĀ® E GF 45 natural (7305)- PET, 45% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

16.500MPa

Strength

200MPa

Impact

65kJ/mĀ²

PRECITEĀ® E GF 45 natural (7305)- PET, 45% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

119202180

AKROMIDĀ®

B3 GF 30 S1 natural (1383)PA6-I GF30

AKROMIDĀ® B3 GF 30 S1 natural (1383) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perfectly suitable for industrial applications and for housings and covers in the automotive industry. The material has a light inherent color.

Features

impact modified

Properties

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
7500 MPa
4200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
125 MPa
70 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
6 %
13 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
6400 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
190 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
10Ā°C | d.a.m.
-
20Ā°C | d.a.m.
-
30Ā°C | d.a.m.
-
40Ā°C | d.a.m.
-
110 kJ/mĀ²
135 kJ/mĀ²
112 kJ/mĀ²
117 kJ/mĀ²
117 kJ/mĀ²
115 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
10Ā°C | d.a.m.
-
20Ā°C | d.a.m.
-
30Ā°C | d.a.m.
-
40Ā°C | d.a.m.
-
35 kJ/mĀ²
40 kJ/mĀ²
25 kJ/mĀ²
25 kJ/mĀ²
25 kJ/mĀ²
20 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,28 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.