Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITEĀ®

Preliminary

P3 black (7811)

PBT

PRECITEĀ® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.600MPa

Strength

60MPa

Impact

90kJ/mĀ²

PRECITEĀ® P3 black (7811) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

AKROMIDĀ®

Preliminary

B3 GF 40 1 black (8353)

PA6 GF40

AKROMIDĀ® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

Modulus

13.000MPa

Strength

195MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

AKROMIDĀ®

C28 GF 25 FRT grey (8331)

PA-Blend

AKROMIDĀ® C28 GF 25 FRT grey (8331) - PA blend, 25% glass fiber, flame retardant, good flowability, NCS S3000N, Public Transportation EN 45545-2.

Modulus

10.800MPa

Strength

140MPa

Impact

47kJ/mĀ²

AKROMIDĀ® C28 GF 25 FRT grey (8331) - PA blend, 25% glass fiber, flame retardant, good flowability, NCS S3000N, Public Transportation EN 45545-2.

AKROMIDĀ®

B3 GF 15 1 L black (4670)

PA6+PP GF15

AKROMIDĀ® B3 GF 15 1 L black (4670) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

5.200MPa

Strength

105MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 GF 15 1 L black (4670) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMIDĀ®

B3 GF 60 4 RM-M black (5238)

PA6+X GF60

AKROMIDĀ® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.

Modulus

22.500MPa

Strength

225MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.

AKROMIDĀ®

B28 GF 15 2 black (7060)

PA6 GF15

AKROMIDĀ® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

Modulus

6.100MPa

Strength

108MPa

Impact

32kJ/mĀ²

AKROMIDĀ® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

PRECITEĀ®

Preliminary

P3 ICF 40 black (6949)

PBT CF 40

PRECITEĀ® P3 ICF 40 black (6949) - PBT, 40% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

31.000MPa

Strength

190MPa

Impact

50kJ/mĀ²

PRECITEĀ® P3 ICF 40 black (6949) - PBT, 40% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

118192080

AKROMIDĀ®

Preliminary

T9 GF 50 black (7601)PPA GF50

AKROMIDĀ® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

Features

heat stabilised 160

Properties

Modulus

17.000MPa

Strength

250MPa

Impact

95kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
17000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
250 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
95 kJ/mĀ²
80 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
16 kJ/mĀ²
14 kJ/mĀ²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
305 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23Ā°C
1,55 g/cmĀ³

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more