AKROTEK®

Preliminary

PPS GF 30 black (8610)PPS GF30

AKROTEK® PPS GF 30 black (8610) is a 30% glass fibre reinforced Polyphenylene sulfide with high rigidity and strength, as well as high temperature and chemical resistance.

Features

hydrolysis / chemically stabilised

Properties

Modulus

12.000MPa

Strength

175MPa

Impact

45kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
12000 MPa
11900 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
175 MPa
175 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,9 %
1,9 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
40°C | d.a.m.
-
45 kJ/m²
45 kJ/m²
45 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
265 °C

Glass transition temperature

ISO 11357-2

DSC, 2nd heating
90 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
280 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

Burning rate 5V

UL 94

3,2 mm Wall thickness
5VA Class

General properties

Density

ISO 1183

23°C
1,55 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,6 %
0,3 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
120 mm
420 mm

MVR

ISO 1133

300°C/5kg
35 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.