PRECITE®

Preliminary

E GF 30 4 black (8622)PET-I GF30

PRECITE® E GF 30 4 black (8622) is a 30% glass fibre reinforced and hydrolysis stabilised Polyethylene terephthalate (PET). It is characterised by a high stiffness and toughness as well as good chemical resistance. This formulation is GMA free (glycidyl methacrylate) and meets the VW-50136 standard. Furthermore, the material impresses with very good dimensional stability due to its low moisture absorption. Therefore, the material is perfectly suitable for technical precision components in applications in the automotive industry, mechanical engineering, E&E and household goods industries with increased humidity.

Features

hydrolysis / chemically stabilised
low warpage
reduced moisture
sports & leisure

Properties

Modulus

9.400MPa

Strength

135MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
9400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
135 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,7 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
14 kJ/m²

Flammability

Flammability

UL 94

0,8 mm Wall thickness
HB Class

General Properties

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,8 - 1,0 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

PRECITE®

P3 GF 30 black (6924)

PBT GF30

PRECITE® P3 GF 30 black (6924) is a 30% glass fiber reinforced PBT with excellent dimensional stability. Thanks to its low moisture absorption, PRECITE® achieves consistent mechanical and electrical properties, even under changing climatic condition

Modulus

10.000MPa

Strength

145MPa

Impact

68kJ/m²

PRECITE®

Preliminary

E GF 30 black (7814)

PET GF30

PRECITE® E GF 30 black (7814) is a 30% glass fibre reinforced, medium viscous polyethylene terephthalate (PET) with high stiffness and toughness even at elevated temperatures. Due to its low moisture absorption, this material is particularly dimensio

Modulus

11.000MPa

Strength

170MPa

Impact

50kJ/m²

PRECITE®

Preliminary

E GF 30 ECO black (8271)

PET GF30

PRECITE® E GF 30 ECO black (8271) is a 30% glass fibre reinforced, medium viscous polyethylene terephthalate (PET) with very high stiffness and toughness as well as high chemical resistance. Due to its low moisture absorption, this material is partic

Modulus

10.500MPa

Strength

170MPa

Impact

45kJ/m²

PRECITE®

Preliminary

K GF 30 4 LA ECO black (8699)

PBT+PET GF30

PRECITE® K GF 30 4 ECO black (8699) is a 30% glass fibre reinforced, hydrolysis stabilised PBT/PET blend with high strength. Due to its low moisture absorption, this material is particularly suitable for precision parts in the automotive, E&E or appl

Modulus

9.500MPa

Strength

120MPa

Impact

65kJ/m²

PRECITE®

Preliminary

P3 GF 30 4 natural (8242)

PBT-I GF30

PRECITE®P3 GF 30 4 natur (8242) is a 30% glass fibre reinforced and hydrolysis stabilised polybutylene terephthalate (PBT). It is characterised by a high stiffness and toughness as well as good chemical resistance. This formulation is GMA free (glyci

Modulus

9.000MPa

Strength

120MPa

Impact

75kJ/m²

AKROMID®

B3 GF 30 RM-M black (3016)

PA6+X GF30

AKROMID® B3 GF 30 RM-M black (3016) is a 30% glass fiber reinforced polyamide 6 with high stiffness and strength. The material is characterised by a lower moisture uptake compared to standard PA 6 GF 30 compounds which results in less mechanical chan

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

PRECITE®

Preliminary

E GF 30 natural (7303)

PET GF30

PRECITE® E GF 30 natural (7303) is a 30% glass fibre reinforced, medium viscous polyethylene terephthalate (PET) with high stiffness and toughness even at elevated temperatures. Due to its low moisture absorption, this material is particularly dimens

Modulus

10.600MPa

Strength

175MPa

Impact

48kJ/m²

PRECITE®

Preliminary

E GF 20 black (7360)

PET GF20

PRECITE® E GF 20 schwarz (7360) is a 20% glass fibre reinforced, medium viscous polyethylene terephthalate (PET) with good stiffness and toughness even at elevated temperatures. Due to its low moisture absorption, this material is particularly dimens

Modulus

7.800MPa

Strength

NA

Impact

35kJ/m²

PRECITE®

Preliminary

E GF 50 black (7395)

PET GF50

PRECITE® E GF 50 black (7395) is a 50% glass fibre reinforced, medium viscous polyethylene terephthalate (PET) with very high stiffness and toughness even at elevated temperatures. Due to its low moisture absorption, this material is particularly dim

Modulus

18.000MPa

Strength

210MPa

Impact

60kJ/m²

PRECITE®

E ICF 30 black (7429)

PET CF30

PRECITE® E ICF 30 black (7429) is medium viscosity polyethylene terephthalate (PET) with 30% recycled carbon fiber. Despite lower density compared to PET with glass fiber reinforcement, the product has very high strength and toughness as well as high

Modulus

26.000MPa

Strength

220MPa

Impact

44kJ/m²

PRECITE®

K GF 30 ECO black (8269)

PBT+PET GF30

PRECITE® K GF 30 ECO black (8269) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish. Due to its low moisture absorption, this material is particularly suitable for precision parts in the automotive, E&E or a

Modulus

10.000MPa

Strength

150MPa

Impact

70kJ/m²

PRECITE®

Preliminary

E GF 45 ECO black (8284)

PET GF45

PRECITE® E GF 45 ECO black (8284) is a 45% glass fibre reinforced, medium viscous polyethylene terephthalate (PET) with very high stiffness and toughness as well as high chemical resistance. Due to its low moisture absorption, this material is partic

Modulus

16.100MPa

Strength

200MPa

Impact

65kJ/m²