PRECITE®

Preliminary

E ICF 30 ECO black (8277)PET CF 30

PRECITE® E ICF 30 ECO black (8277) is a 30% carbon fibre reinforced, medium viscous polyethylene terephthalate (PET) with very high stiffness and toughness as well as high dimensionalstability and chemical resistance. The formulations of the sustainable ECO products are partly based on regenerated post-consumer feedstock saving valuable natural resources.

Features

recycled content
reduced moisture
antistatic/conductive
metal substitution
lightweight construction
sustainable
CO2eq reduced

Properties

Modulus

23.700MPa

Strength

215MPa

Impact

50kJ/m²

Sustainability

Recycled content

ISO 14021

Post-consumer (PCR)
55 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
23700 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
215 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,3 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
50 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
7 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
250 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

General Properties

Density

ISO 1183

23°C
1,45 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,1 - 0,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

PRECITE®

E ICF 30 black (7429)

PET CF30

PRECITE® E ICF 30 black (7429) is medium viscosity polyethylene terephthalate (PET) with 30% recycled carbon fiber. Despite lower density compared to PET with glass fiber reinforcement, the product has very high strength and toughness as well as high

Modulus

26.000MPa

Strength

220MPa

Impact

44kJ/m²

PRECITE®

Preliminary

E GF 30 ECO black (8271)

PET GF30

PRECITE® E GF 30 ECO black (8271) is a 30% glass fibre reinforced, medium viscous polyethylene terephthalate (PET) with very high stiffness and toughness as well as high chemical resistance. Due to its low moisture absorption, this material is partic

Modulus

10.500MPa

Strength

170MPa

Impact

45kJ/m²

PRECITE®

Preliminary

E GF 45 ECO black (8284)

PET GF45

PRECITE® E GF 45 ECO black (8284) is a 45% glass fibre reinforced, medium viscous polyethylene terephthalate (PET) with very high stiffness and toughness as well as high chemical resistance. Due to its low moisture absorption, this material is partic

Modulus

16.100MPa

Strength

200MPa

Impact

65kJ/m²

PRECITE®

Preliminary

K GF 30 ECO black (8269)

PBT+PET GF30

PRECITE® K GF 30 ECO black (8269) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish. Due to its low moisture absorption, this material is particularly suitable for precision parts in the automotive, E&E or a

Modulus

10.000MPa

Strength

150MPa

Impact

70kJ/m²

PRECITE®

Preliminary

K GF 30 4 LA ECO black (8699)

PBT+PET GF30

PRECITE® K GF 30 4 ECO black (8699) is a 30% glass fibre reinforced, hydrolysis stabilised PBT/PET blend with high strength. Due to its low moisture absorption, this material is particularly suitable for precision parts in the automotive, E&E or appl

Modulus

9.500MPa

Strength

120MPa

Impact

65kJ/m²

PRECITE®

Preliminary

K GF 10 ECO black (8696)

PBT+PET GF10

PRECITE® K GF 10 ECO black (8696) is a 10% glass fibre reinforced PBT/PET blend with high strength and improved surface finish. Due to its low moisture absorption, this material is particularly suitable for precision parts in the automotive, E&E or a

Modulus

4.800MPa

Strength

100MPa

Impact

25kJ/m²

PRECITE®

Preliminary

P3 ICF 30 black (6948)

PBT CF30

PRECITE® P3 ICF 30 black (6948) is a PBT reinforced with 30% recycled carbon fiber with excellent dimensional stability. Thanks to its low moisture absorption, PRECITE® achieves consistent mechanical and electrical properties, even under changing cl

Modulus

23.500MPa

Strength

175MPa

Impact

50kJ/m²

PRECITE®

Preliminary

E GF 30 black (7814)

PET GF30

PRECITE® E GF 30 black (7814) is a 30% glass fibre reinforced, medium viscous polyethylene terephthalate (PET) with high stiffness and toughness even at elevated temperatures. Due to its low moisture absorption, this material is particularly dimensio

Modulus

11.000MPa

Strength

170MPa

Impact

50kJ/m²

AKROMID®

Preliminary

A3 GF 30 6 ECO black (8160)

PA66 GF30

AKROMID® A3 GF 30 6 ECO black (8160) is a 30% glass fibre-reinforced, inorganically heat-stabilised polyamide 6.6. The compound is suitable for technical components in mechanical engineering and the automotive industry with demands for high stiffness

Modulus

9.000MPa

Strength

150MPa

Impact

50kJ/m²

AKROMID®

Preliminary

B3 GF 30 1 L ECO black (8967)

PA6+PP GF30

AKROMID® B3 GF 30 1 L ECO black (8967) is a PA6+PP blend with post consumer recycled content and reduced density. With 30% glass fiber reinforcement this material is suitable for components with high strength and stiffness where weight reduction is r

Modulus

9.000MPa

Strength

140MPa

Impact

57kJ/m²

AKROMID®

Preliminary

B3 GF 15 ECO black (9171)

PA6 GF30

AKROMID® B3 GF 15 ECO black (9171) is a 15% glass fibre-reinforced, heat-stabilised polyamide 6 with a basic laser markability. The formulation of this sustainable ECO product is partly based on post-consumer recycled feedstock and thus contribute to

Modulus

6.300MPa

Strength

120MPa

Impact

35kJ/m²

AKROMID®

Preliminary

B3 GF 30 ECO black (9172)

PA6 GF30

AKROMID® B3 GF 30 ECO black (9172) is a 30% glass fibre-reinforced, heat-stabilised polyamide 6 with a basic laser markability. The formulation of this sustainable ECO product is partly based on post-consumer recycled feedstock and thus contribute to

Modulus

10.000MPa

Strength

160MPa

Impact

60kJ/m²