PRECITE®

K GF 30 black (7249)PBT+PET GF30

PRECITE K GF 30 black (7249) is a 30% glass fibre reinforced PBT/PET blend with higher strength and improved surface finish compared with PBT compounds

Properties

Modulus

9.800MPa

Strength

150MPa

Impact

65kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
9800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
150 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,1 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
10 kJ/m²

Flammability

Flammability

UL 94

0,8 mm Wall thickness
HB Class

General Properties

Density

ISO 1183

23°C
1,55 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

PRECITE®

K GF 30 ECO black (8269)

PBT+PET GF30

PRECITE® K GF 30 ECO black (8269) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish. Due to its low moisture absorption, this material is particularly suitable for precision parts in the automotive, E&E or a

Modulus

10.000MPa

Strength

150MPa

Impact

70kJ/m²

PRECITE®

Preliminary

K GF 30 4 LA ECO black (8699)

PBT+PET GF30

PRECITE® K GF 30 4 ECO black (8699) is a 30% glass fibre reinforced, hydrolysis stabilised PBT/PET blend with high strength. Due to its low moisture absorption, this material is particularly suitable for precision parts in the automotive, E&E or appl

Modulus

9.500MPa

Strength

120MPa

Impact

65kJ/m²

PRECITE®

Preliminary

K GF 10 ECO black (8696)

PBT+PET GF10

PRECITE® K GF 10 ECO black (8696) is a 10% glass fibre reinforced PBT/PET blend with high strength and improved surface finish. Due to its low moisture absorption, this material is particularly suitable for precision parts in the automotive, E&E or a

Modulus

4.800MPa

Strength

100MPa

Impact

25kJ/m²

AKROMID®

B3 GF 30 S1 black (1281)

PA6-I GF30

AKROMID® B3 GF 30 S1 black (1281) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perfec

Modulus

8.800MPa

Strength

150MPa

Impact

85kJ/m²

AKROMID®

A3 GF 30 S1 black (1365)

PA66-I GF30

AKROMID® A3 GF 30 S1 black (1365) is a 30% glass fiber reinforced, impact modified Polyamide 6.6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6.6 GF 30. The material is perfectly su

Modulus

9.300MPa

Strength

180MPa

Impact

100kJ/m²

AKROMID®

B3 GF 30 S1 black (2091)

PA6-I GF30

AKROMID® B3 GF 30 S1 black (2091) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perfec

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/m²

AKROMID®

A3 GF 25 1 black (2384)

PA66 GF25

AKROMID® A3 GF 25 1 black (2384) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength.

Modulus

8.500MPa

Strength

175MPa

Impact

70kJ/m²

AKROMID®

A3 GF 30 1 black (2385)

PA66 GF30

AKROMID® A3 GF 30 1 black (2385) is a 30% glass fiber reinforced polyamide 6.6. It is characterised by high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engine

Modulus

10.000MPa

Strength

190MPa

Impact

60kJ/m²

AKROMID®

B3 GF 25 1 black (2484)

PA6 GF25

PLACEHOLDER

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²

AKROMID®

B3 GF 30 black (2493)

PA6 GF30

PLACEHOLDER

Modulus

10.300MPa

Strength

185MPa

Impact

85kJ/m²

AKROMID®

B3 GF 30 1 black (2485)

PA6 GF30

AKROMID® B3 GF 30 1 black (2485) is a 30% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engine

Modulus

10.300MPa

Strength

175MPa

Impact

80kJ/m²

AKROLOY®

PA GF 30 black (2718)

PA66+PA6I/6T

AKROLOY® PA GF 30 black (2718) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 30 black (6415) with a modern stabiliza

Modulus

10.500MPa

Strength

210MPa

Impact

80kJ/m²