AKROMID®

Preliminary

B3 GF 40 1 black (8353)

PA6 GF40

AKROMID® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

Modulus

13.000MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 40 1 black (8353) - PA 6, 40% glass fiber reinforced with excellent bonding to LSR, low emission and heat stabilised

AKROMID®

B3 GF 60 4 RM-M natural (4645)

PA6 + X GF60

AKROMID® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.

Modulus

21.500MPa

Strength

235MPa

Impact

65kJ/m²

AKROMID® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.

AKROMID®

B3 GF 50 black (4907)

PA6 GF50

AKROMID® B3 GF 50 black (4907) - PA6.6, 50% glass fiber, easy flow, high rigidity and strength

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (4907) - PA6.6, 50% glass fiber, easy flow, high rigidity and strength

AKROLOY®

PA ICF 30 black (5269)

PA66+PA6I/6T CF30

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

25.000MPa

Strength

220MPa

Impact

50kJ/m²

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

B3 GF 30 1 EN black (5637)

PA6 GF30

AKROMID® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B28 LGF 40 1 L black (6155)

PA6 + PP LGF40

AKROMID® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

Modulus

12.000MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID® B28 LGF 40 1 L black (6155) - PA6/PP-Blend, 40% long glass fiber reinforced, easy flowing, lightweight, low shrinkage, very good fatigue performance

AKROLOY®

PA GF 40 black (6416)

PA66+PA6I/6T GF40

AKROLOY® PA GF 40 black (6416) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

13.000MPa

Strength

235MPa

Impact

95kJ/m²

AKROLOY® PA GF 40 black (6416) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

118192080

AKROTEK®

PK-HM 8 black (6246)PK

AKROTEK® PK-HM 8 black (6246) is an unreinforced, high viscosity polyketone. The material is suitable for drinking water contact and meets the requirements according to ACS and WRAS. Moreover the material corresponds to the European food guideline EU 10/2011, but not to the American FDA 21 CFR.

Features

hydrolysis / chemically stabilised

Regulatory

acseu102011wras

Properties

Modulus

1.600MPa

Strength

60MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
1600 MPa
1600 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
60 MPa
60 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
21 %
21 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 300 %
> 300 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
1700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
62 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
21 kJ/m²
21 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
100 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,24 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,8 - 0,9 %

Water absorption

ISO 62

23°C, saturated
2,0 - 2,4 %

Molding shrinkage

ISO 294-4

flow
transverse
1,7 - 1,9 %
1,9 - 2,1 %

Rheological Properties

MVR

ISO 1133

240°C/2,16kg
6 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.